Semiconductor device with extension structure and method for fabricating the same

ABSTRACT

A semiconductor device includes a semiconductor region, a source region, a drain region, a source extension region a drain extension region, a first gate insulation film, a second gate insulation film, and a gate electrode. The source region, drain region, source extension region and drain extension region are formed in a surface portion of the semiconductor region. The first gate insulation film is formed on the semiconductor region between the source extension region and the drain extension region. The first gate insulation film is formed of a silicon oxide film or a silicon oxynitride film having a nitrogen concentration of 15 atomic % or less. The second gate insulation film is formed on the first gate insulation film and contains nitrogen at a concentration of between 20 atomic % and 57 atomic %. The gate electrode is formed on the second gate insulation film.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of application Ser. No. 12/757,658, filed Apr. 9, 2010 now U.S. Pat. No. 7,989,903, which is a continuation of application Ser. No. 11/704,924, filed Feb. 12, 2007 now U.S. Pat. No. 7,781,848, which is based upon and claims the benefit of priority from prior Japanese Patent Application No. 2006-037107, filed Feb. 14, 2006, the entire contents of all of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a semiconductor device with reduced dimensions and a method for fabricating the semiconductor device. The invention relates, for example, to an insulated-gate transistor including a semiconductor gate electrode which is formed of, e.g., polycrystalline silicon (Si). In addition, the invention relates to a semiconductor device with a very fine structure, which includes an array of a great number of basic elements each formed of the above-mentioned insulated-gate transistor, and to a method for fabricating the semiconductor device.

2. Description of the Related Art

In a MOS integrated circuit, for instance, insulated-gate transistors are employed as basic elements. In a semiconductor device in which such basic elements are integrated at high density on a semiconductor chip, a parasitic resistance and a short-channel effect in each insulated-gate transistor increase as the basic elements become smaller in size. It is thus important to form the source/drain region of the insulated-gate transistor so that the source/drain region may have a low resistance and be shallow. In order to lower the resistance of an impurity diffusion region, it is necessary to sufficiently activate the impurity elements that are doped in the impurity diffusion region by, e.g., ion implantation. On the other hand, the impurity elements are diffused in the semiconductor region by annealing for activation (hereinafter referred to as an “activation annealing process”). It is thus necessary to perform the activation annealing process at high temperatures and at high speed.

As a method for instantaneously supplying thermal energy necessary for activating impurity elements, an optical annealing technique has been studied which employs a flashtube in which a rare gas such as xenon (Xe) is sealed, or a laser. Since the light source, which is used in the optical annealing technique, can emit light with a pulse width on the order of milliseconds, it is possible to activate the doped impurity ions with little diffusion. In the optical annealing technique, by increasing the irradiation light energy, the sheet resistance of the impurity diffusion layer can greatly be reduced and the defects due to ion implantation can be remedied. As a result, an enhancement in driving power of the insulated-gate transistor can be expected.

However, in the optical annealing technique, since high thermal energy is supplied instantaneously, heat tends not to escape from the polycrystalline Si on the gate insulation film and the temperature of the polycrystalline Si tends to increase. In particular, the following problem arises with an n-channel type insulated-gate transistor such as an nMOSFET. That is, in the activation annealing process using the optical annealing technique, the withstand voltage of the gate insulation film deteriorates before sufficient thermal energy is supplied to a single-crystal Si substrate. As a result, gate leakage current of the nMOSFET increases.

In order to solve this problem, Jpn. Pat. Appln. KOKAI Publication No. 2004-63574, for instance, discloses a method in which the dosage of impurities, which are ion-implanted in the polycrystalline Si layer, is reduced, or the kind of impurities is changed. According to this method, however, capacitance forms due to depletion in a bottom part of the gate electrode that is formed of polycrystalline Si. As a result, the driving performance of the insulated-gate transistor deteriorates.

In short, there is a trade-off between the increase in impurity density (high concentration activation) in the source/drain region and gate electrode of the insulated-gate transistor, which includes the gate electrode formed of polycrystalline Si, and the suppression of the gate leakage current. Hence, in the activation annealing process using the conventional optical annealing technique, it has been difficult to secure a process window relating to the heat treatment step in the fabrication of the semiconductor device with the very fine structure, for which a shallow junction is required.

BRIEF SUMMARY OF THE INVENTION

A semiconductor device according to an aspect of the present invention includes:

a semiconductor region of a first conductivity type;

a source region of a second conductivity type which is formed in a surface portion of the semiconductor region;

a drain region of the second conductivity type which is formed in a surface portion of the semiconductor region and is apart from the source region;

a source extension region of the second conductivity type which is formed in a surface portion of the semiconductor region between the source region and the drain region, is in contact with the source region and is apart from the drain region, the source extension region having a depth from a surface of the semiconductor region, which is less than a depth of the source region from the surface of the semiconductor region;

a drain extension region of the second conductivity type which is formed in a surface portion of the semiconductor region between the source extension region and the drain region, is in contact with the drain region and is apart from the source extension region, the drain extension region having a depth from the surface of the semiconductor region, which is less than a depth of the drain region from the surface of the semiconductor region;

a first gate insulation film which is formed on the semiconductor region between the source extension region and the drain extension region and is formed of a silicon oxide film or a silicon oxynitride film having a nitrogen concentration of 15 atomic % or less;

a second gate insulation film which is formed on the first gate insulation film and contains nitrogen at a concentration of between 20 atomic % and 57 atomic %; and

a gate electrode which is formed of a semiconductor material of the second conductivity type on the second gate insulation film.

A method for fabricating a semiconductor device according to an aspect of the present invention includes:

forming a gate insulation film on a semiconductor region of a first conductivity type;

forming a semiconductor layer on the gate insulation film;

forming a gate electrode by selecting etching the semiconductor layer;

doping a first impurity element of a second conductivity type in the semiconductor region in a self-alignment manner, by using the gate electrode as a mask;

performing a first annealing process for activating the first impurity element and forming a source region of the second conductivity type and a drain region of the second conductivity type, between which a part of the semiconductor region is interposed;

forming sidewall spacers on side walls of the gate electrode;

doping a second impurity element of the second conductivity type in the semiconductor region in a self-alignment manner, by using the gate electrode and the sidewall spacers as a mask; and

performing a second annealing process for activating the second impurity element and forming, in the semiconductor region between the source region and the drain region, a source extension region of the second conductivity type having a depth from a surface of the semiconductor region, which is smaller than a depth of the source region from the surface of the semiconductor region, and a drain extension region of the second conductivity type having a depth from the surface of the semiconductor region, which is smaller than a depth of the drain region from the surface of the semiconductor region, the first annealing process and the second annealing process being performed in a temperature range of 1273 K to 1600 K for a heat treatment time which is specified in a range in a double-logarithmic graph with an upper limit expressed by t=3×10⁻¹⁵ exp(49000/T) and a lower limit expressed by t=3×10⁻¹⁷ exp(49000/T), where t is a heat treatment time and T is a heat treatment temperature (K).

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING

FIG. 1 is a cross-sectional view that schematically shows a part of the structure of a semiconductor device according to a first embodiment of the present invention;

FIGS. 2 to 5 are cross-sectional views illustrating first to fourth fabrication steps of the semiconductor device according to the first embodiment of the invention;

FIG. 6 is a graph showing the relationship between heat treatment temperature and heat treatment time, which are suitable for activation annealing in the first embodiment of the invention;

FIGS. 7 to 18 are cross-sectional views illustrating fourth to 15th fabrication steps of the semiconductor device according to the first embodiment of the invention;

FIG. 19 is a circuit diagram showing a measuring circuit of a gate leakage current in an n-channel insulated-gate transistor;

FIG. 20 is a plan view of a gate electrode of the n-channel insulated-gate transistor which is the object of measurement by the measuring circuit shown in FIG. 19;

FIG. 21 is a graph showing the relationship between gate leakage currents and cumulative distributions of devices in connection with n-channel insulated-gate transistors according to the first embodiment and comparative examples;

FIG. 22 is a graph showing impurity profiles in extension regions of the n-channel insulated-gate transistors according to the first embodiment and a comparative example;

FIG. 23 is a graph showing the relationship between impurity densities of As and P and gate leakage current in an n-channel insulated-gate transistor;

FIG. 24 is a graph showing the relationship between gate leakage current and sheet resistance in the extension region in the n-channel insulated-gate transistor in the case where P and As are used as dopants in the gate electrode;

FIG. 25 is a graph showing the relationship between gate leakage current and sheet resistance of the extension region, with an auxiliary heating temperature of the silicon substrate being used as a parameter;

FIGS. 26 to 33 are cross-sectional views illustrating first to eighth fabrication steps of a semiconductor device according to a second modification of the first embodiment of the invention;

FIG. 34 is a cross-sectional view that schematically shows a part of the structure of a semiconductor device according to a second embodiment of the present invention;

FIG. 35 is an enlarged view of an insulated-gate transistor, and illustrates the function of an offset spacer;

FIG. 36 is an enlarged view of FIG. 34, and illustrates the function of the offset spacer;

FIGS. 37 to 47 are cross-sectional views illustrating first to eleventh fabrication steps of the semiconductor device according to the second embodiment of the invention;

FIG. 48 is a graph showing the relationship between gate leakage currents and cumulative distributions of devices in connection with n-channel insulated-gate transistors according to the first embodiment and comparative examples;

FIG. 49 is a graph showing impurity profile is extension regions of the n-channel insulated-gate transistors according to the second embodiment and comparative examples;

FIG. 50 is a graph showing the relationship between gate leakage current and gate overlap capacitance in the n-channel insulated-gate transistors

FIG. 51 is a graph showing the relationship between drain voltage and drain current in n-channel insulated-gate transistors according to the second embodiment and a comparative example;

FIG. 52 is a graph showing the relationship between gate voltage and drain current in the n-channel insulated-gate transistors according to the second embodiment and the comparative example;

FIGS. 53 to 59 are cross-sectional views illustrating first to seventh fabrication steps of a semiconductor device according to a modification of a second embodiment of the invention;

FIG. 60 is a cross-sectional view that schematically shows a part of the structure of a semiconductor device according to a third embodiment of the present invention;

FIG. 61 is a graph showing the relationship between gate leakage currents and cumulative distributions of devices in connection with n-channel insulated-gate transistors according to the third embodiment and comparative examples;

FIG. 62 is a graph showing the relationship between gate leakage currents and cumulative distributions of devices in connection with p-channel insulated-gate transistors according to the third embodiment and comparative examples;

FIG. 63 is a graph showing the relationship between gate length and gate threshold voltage in the n-channel insulated-gate transistors according to the third embodiment of the invention;

FIG. 64 is a graph showing the relationship between gate length and gate threshold voltage in the p-channel insulated-gate transistors according to the third embodiment of the invention;

FIGS. 65 to 81 are cross-sectional views illustrating first to 17th fabrication steps of the semiconductor device according to the third embodiment of the invention;

FIG. 82 is a cross-sectional view that schematically shows a part of the structure of a semiconductor device according to a fourth embodiment of the present invention;

FIGS. 83 to 97 are cross-sectional views illustrating first to 15th fabrication steps of the semiconductor device according to the fourth embodiment of the invention;

FIG. 98 is a cross-sectional view that schematically shows a part of the structure of a semiconductor device according to a fifth embodiment of the present invention;

FIG. 99 is a graph showing a distribution of a nitrogen concentration in a first gate insulation film and a second gate insulation film in the semiconductor device according to the fifth embodiment of the invention;

FIG. 100 is a graph showing the relationship between gate leakage current and gate depletion ratio in the n-channel insulated-gate transistors according to the fifth embodiment of the invention and conventional n-channel insulated-gate transistors;

FIG. 101 is a cross-sectional view that schematically shows a part of the structure of a semiconductor device according to a sixth embodiment of the present invention;

FIG. 102 is a graph showing the relationship between gate leakage current and gate depletion ratio in the n-channel insulated-gate transistors according to the sixth embodiment of the invention and conventional n-channel insulated-gate transistors;

FIG. 103 is a cross-sectional view that schematically shows a part of the structure of a semiconductor device according to a seventh embodiment of the present invention;

FIG. 104 is a diagram showing covalent bond radii of Group III to Group V elements;

FIG. 105 is a graph showing variations in gate depletion ratio and gate leakage current when the ratio of impurities of an opposite conductivity type (p-type) to impurities of a major conductivity type (n-type) is varied;

FIG. 106 is a graph showing the relationship between gate leakage current and gate depletion ratio in n-channel insulated-gate transistors according to the seventh embodiment of the invention and conventional n-channel insulated-gate transistors;

FIG. 107 is a graph showing the relationship between on-current and off-current in the n-channel insulated-gate transistors according to the seventh embodiment of the invention and conventional n-channel insulated-gate transistors;

FIG. 108 is a graph showing the relationship between gate length and gate threshold voltage in the n-channel insulated-gate transistors according to the seventh embodiment of the invention and conventional n-channel insulated-gate transistors;

FIG. 109 is a graph showing a nitrogen concentration profile in gate insulation films in an n-channel insulated-gate transistor according to a first modification of the fifth embodiment of the invention;

FIG. 110 is a graph showing a nitrogen concentration profile in gate insulation films in an n-channel insulated-gate transistor according to a second modification of the fifth embodiment of the invention;

FIG. 111 is a cross-sectional view of a semiconductor device according to a third modification of the fifth embodiment of the invention;

FIG. 112 is a cross-sectional view of a semiconductor device according to a fourth modification of the fifth embodiment of the invention;

FIG. 113 is a cross-sectional view of a semiconductor device according to a fifth modification of the fifth embodiment of the invention;

FIG. 114 is a cross-sectional view of a semiconductor device according to a first modification of the sixth embodiment of the invention;

FIG. 115 is a cross-sectional view of a semiconductor device according to a second modification of the sixth embodiment of the invention;

FIG. 116 is a cross-sectional view of a semiconductor device according to a third modification of the sixth embodiment of the invention;

FIG. 117 is a cross-sectional view of a semiconductor device according to a fourth modification of the sixth embodiment of the invention;

FIG. 118 is a cross-sectional view of a semiconductor device according to a first modification of the seventh embodiment of the invention;

FIG. 119 is a cross-sectional view of a semiconductor device according to a second modification of the seventh embodiment of the invention;

FIG. 120 is a cross-sectional view of a semiconductor device according to a third modification of the seventh embodiment of the invention;

FIG. 121 is a cross-sectional view of a semiconductor device according to a fourth modification of the seventh embodiment of the invention; and

FIG. 122 is a cross-sectional view of a semiconductor device according to a fifth modification of the seventh embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

First to seventh embodiments of the present invention will now be described with reference to the accompanying drawings. In the drawings, the same or similar parts are denoted by the same or like reference numerals. It should be noted, however, that the drawings are schematic ones, and the relationship between thickness and plan-view dimensions, the ratio of thicknesses of respective layers, etc., are different from actual ones. The specific thicknesses, dimensions, etc., should be determined in consideration of the descriptions below. Needless to say, the relationship or ratio in dimensions is partly different between the drawings. First to seventh embodiments, which will be described below, are mere examples of devices and methods which embody the technical concept of the present invention, and the materials, shapes, structures and arrangements of the structural parts, for instance, are not limited to those in the embodiments below.

(First Embodiment)

In the description below of a first embodiment of the invention, a first conductivity type and a second conductivity type are mutually opposite conductivity types. In the description of the first embodiment and modifications thereof, it is assumed that the first conductivity type is p-type and the second conductivity type is n-type. Alternatively, the first conductivity type may be n-type and the second conductivity type may be p-type. FIG. 1 is a cross-sectional view of a semiconductor device according to the first embodiment of the invention.

As shown in FIG. 1, the semiconductor device has a CMOS structure including an nMOSFET and a pMOSFET. Specifically, a semiconductor region (p-well region) 2 of a first conductivity type (p-type) and a semiconductor region (n-well region) 3 of a second conductivity type (n-type), which are adjacent to each other, are formed on an upper surface portion of a silicon (Si) substrate 1 of the first conductivity type (p-type). An nMOSFET is formed on the p-well region 2 and a pMOSFET is formed on the n-well region 3.

The CMOS structure becomes, for example, a basic device of a semiconductor integrated circuit such as an LSI. Although not shown, the p-well region 2 and n-well region 3 are so formed as to extend in a direction perpendicular to the sheet surface of FIG. 1. In other words, the p-well region 2 and n-well region 3 are formed such that their plan-view patterns have stripe shapes. For example, a cyclic structure, such as a gate array, is formed. Regardless of the cyclic arrangement or non-cyclic arrangement, various plan-view layouts can be adopted.

Device isolation regions 4 are formed in surface portions of the n-well region 3 and p-well region. The device isolation regions 4 are so formed as to surround the n-well region 3 and p-well region 2 in such a fashion that their upper surfaces (plan-view patterns) have rectangular ring shapes (picture-frame shapes). Regions surrounded by the device isolation regions 4 become insular active regions AA. The nMOSFET and pMOSFET are formed on the active regions AA of the p-well region 2 and n-well region 3, respectively. The active regions, which appear on the cross section of FIG. 1, are electrically insulated by the device isolation regions 4 from other active regions AA which neighbor in a direction perpendicular to the sheet surface of FIG. 1.

Next, the structures of the nMOSFET and pMOSFET are described. To begin with, the nMOSFET is described. As shown in FIG. 1, a source region 9 a and a drain region 9 b, which are of the second conductivity type (n-type), are formed in upper surface portions of the p-well region 2 and are opposed to each other so as to sandwich an upper surface portion of the p-well region 2, which becomes a channel region. The source region 9 a and drain region 9 b extend in the direction perpendicular to the sheet surface of FIG. 1. A source extension region 11 a and a drain extension region 11 b, which are of the second conductivity type (n-type) and have shallower junctions than the source region 9 a and drain region 9 b, are formed at front faces of the source region 9 a and drain region 9 b, which are opposed to the channel region. Thereby, a lightly doped drain (LDD) structure is formed. In the LDD structure, the effective gate length of the nMOSFET is defined by the length of the p-well region 2 between the source extension region 11 a and drain extension region 11 b. The source extension region 11 a and drain extension region 11 b extend in the direction perpendicular to the sheet surface of FIG. 1. The gate width of the nMOSFET is defined by the lengths of the source extension region 11 a and drain extension region 11 b which extend in the direction perpendicular to the sheet surface of FIG. 1. The junction depth of each of the source extension region 11 a and drain extension region 11 b is set at 20 nm or less.

A gate insulation film 5 n of the nMOSFET is formed on the surface of the p-well region 2 which becomes the channel region between the source extension region 11 a and drain extension region 11 b. A gate electrode 7 n, which is formed of a polycrystalline Si film or a polycrystalline SiGe (Ge concentration: 10 to 30 atomic %) film, is formed on the gate insulation film 5 n. In the description below, the term “semiconductor polycrystalline film” is used to refer to the concept including a polycrystalline Si film and a polycrystalline SiGe film. The semiconductor polycrystalline film may include a composite film of the polycrystalline Si film and polycrystalline SiGe film, and may further include polycrystalline films of other semiconductors such as SiC and SiSn. Phosphorus (P) is doped in the gate electrode 7 n at an impurity density of about 1×10²⁰ cm⁻³ to 5×10²⁰ cm⁻³. Preferably, P is doped in the gate electrode 7 n at an impurity density of about 1×10²⁰ cm⁻³ to 4×10²⁰ cm⁻³. More preferably, P, together with arsenic (As) or antimony (Sb), is doped in the gate electrode 7 n which is formed of a semiconductor polycrystalline film, and the total dosage is, in terms of impurity density, about 1×10²⁰ cm⁻³ to 5×10²⁰ cm⁻³, and more preferably about 1×10²⁰ cm⁻³ to 4×10²⁰ cm⁻³. In addition, it is preferable that the impurity density of As or Sb be higher than that of P so that As or Sb may become a major component in the gate electrode 7 n. Sidewall spacers 21 n are formed of silicon oxide films on the side surfaces of the gate electrode 7 n and gate insulation film 5 n of the nMOSFET so as to sandwich the gate electrode 7 n and gate insulation film 5 n. Further, sidewall spacers 22 n are formed of silicon nitride films on the side surfaces of the sidewall spacers 21 n so as to sandwich the sidewall spacers 21 n.

Next, the structure of the pMOSFET is described. As shown in FIG. 1, a drain region 10 a and a source region 10 b, which are of the first conductivity type (p-type), are formed in upper surface portions of the n-well region 3 and are opposed to each other so as to sandwich an upper surface portion of the n-well region 3, which becomes a channel region. The drain region 10 a and source region 10 b extend in the direction perpendicular to the sheet surface of FIG. 1. A drain extension region 12 a and a source extension region 12 b, which are of the first conductivity type (p-type) and have shallower junctions than the drain region 10 a and source region 10 b, are formed at front faces of the drain region 10 a and source region 10 b, which are opposed to the channel region. Thereby, an LDD structure is formed. In the LDD structure, the effective gate length of the pMOSFET is defined by the length of the n-well region 3 between the drain extension region 12 a and source extension region 12 b. The drain extension region 12 a and source extension region 12 b extend in the direction perpendicular to the sheet surface of FIG. 1. The gate width of the pMOSFET is defined by the lengths of the drain extension region 12 a and source extension region 12 b which extend in the direction perpendicular to the sheet surface of FIG. 1. The junction depth of each of the drain extension region 12 a and source extension region 12 b is also set at 20 nm or less.

A gate insulation film 5 p is formed on the surface of the n-well region 3 which becomes the channel region between the drain extension region 12 a and source extension region 12 b of the pMOSFET. A gate electrode 7 p is formed of a semiconductor polycrystalline film on the gate insulation film 5 p. Boron (B) is doped in the gate electrode 7 p, which is formed of the semiconductor polycrystalline film, at an impurity density of about 1×10²⁰ cm⁻³ to 5×10²⁰ cm⁻³, and more preferably at an impurity density of about 1×10²⁰ cm⁻³ to 4×10²⁰ cm⁻³. A pair of sidewall spacers 21 p are formed of silicon oxide films on the side surfaces of the gate electrode 7 p and gate insulation film 5 p of the pMOSFET so as to sandwich the gate electrode 7 p and gate insulation film 5 p. Further, sidewall spacers 22 p are formed so as to sandwich the outer surfaces of the pair of opposed sidewall spacers 21 p.

In the above-described nMOSFET and pMOSFET, the sidewall spacers of the stacked structure including the silicon oxide film 21 n, 21 p and silicon nitride film 22 n, 22 p may be replaced with sidewall spacers of a single-layer structure including only the silicon oxide film or the silicon nitride film. The thickness of the insulation film, which becomes the sidewall spacer, is set at 20 to 40 nm as a total thickness of the silicon oxide film and silicon nitride film combined. The sidewall spacers 21 n, 21 p, 21 p, 22 p function to prevent a metal silicide reaction in a saliciding process.

Further, in the above-described nMOSFET and pMOSFET, a silicide (NiSi_(x), CoSi_(x), PtSi_(x), PdSi_(x), WSi_(x), TiSi_(x), MoSi_(x)) layer 31 a of a high-melting-point metal, such as nickel (Ni), cobalt (Co), platinum (Pt), palladium (Pd), tungsten (W), titanium (Ti) or molybdenum (Mo), is formed on the surface of the source region 9 a, and a similar metal silicide layer 31 b is formed on the surface of the drain region 9 b. In like manner, a metal silicide layer 32 a is formed on the surface of the drain region 10 a, and a metal silicide layer 32 b is formed on the surface of the source region 10 b. Moreover, a metal silicide layer 33 n is formed on top of the gate electrode in of the nMOSFET, and a metal silicide layer 33 p is formed on top of the gate electrode 7 p of the pMOSFET. Thereby, each of the nMOSFET and pMOSFET forms a salicide structure.

An interlayer insulation film 24 is formed over the silicon substrate 1 so as to cover the nMOSFET and pMOSFET having the above-described structures. A wiring 43 a for the nMOSFET is connected to the metal silicide layer 31 a via a contact plug 41 a which is buried in a contact hole that is made in the interlayer insulation film 24. To be more specific, the wiring 43 a for the nMOSFET is electrically connected to the source region 9 a of the nMOSFET. In addition, a wiring 43 b for the nMOSFET is connected to the metal silicide layer 31 b via a contact plug 41 b which is buried in a contact hole that is made in the interlayer insulation film 24. To be more specific, the wiring 43 b for the nMOSFET is electrically connected to the drain region 9 b of the nMOSFET.

Besides, a wiring 44 a for the pMOSFET is connected to the metal silicide layer 32 a via a contact plug 42 a which is buried in a contact hole that is made in the interlayer insulation film 24. To be more specific, the wiring 44 a for the pMOSFET is electrically connected to the drain region 10 a of the pMOSFET. In addition, a wiring 44 b for the pMOSFET is connected to the metal silicide layer 32 b via a contact plug 42 b which is buried in a contact hole that is made in the interlayer insulation film 24. To be more specific, the wiring 44 b for the pMOSFET is electrically connected to the source region 10 b of the pMOSFET.

Although not shown, on the far side of the sheet surface of FIG. 1, a gate wiring is connected to the metal silicide layer 33 n, 33 p on top of the gate electrode 7 n, 7 p via a contact plug which is buried in a contact hole formed in the interlayer insulation film 24.

In the semiconductor device according to the first embodiment of the present invention, the dosage of P in the gate electrode 7 n of the semiconductor polycrystalline film of the nMOSFET is reduced to about 5×10²⁰ cm⁻³ or less, preferably about 4×10²⁰ cm⁻³. Thus, pile-up or punch-through of P to the gate insulation film 5 n can be suppressed. Hence, in a method for fabricating the semiconductor device according to the first embodiment of the invention, as will be described later, the irradiation energy of very rapid optical annealing can be increased. As a result, it becomes possible to perform, while suppressing gate leakage current, high-concentration activation and defect remedy in the source extension region 11 a, 12 b and the drain extension region 11 b, 12 a. Therefore, the process window relating to the heat treatment step in the method for fabricating the semiconductor device according to the first embodiment is increased, and the high-performance, fine-structure semiconductor device can easily be provided.

Next, referring to FIGS. 2 to 18, a method for fabricating the semiconductor device according to the first embodiment of the invention is described. FIGS. 2 to 18, excluding FIG. 6, are cross-sectional views which successively illustrate fabrication steps of the semiconductor device shown in FIG. 1. The method for fabricating the semiconductor device which will be described below, is merely an example, and the semiconductor device may also be fabricated by other various fabrication methods including modification of this method. For example, in the description below, a salicide (self-aligned silicide) structure is realized by using Ni silicide (Ni₂Si, NiSi_(x)) as an example of a silicide of a high-melting-point metal. Needless to say, other silicides, such as CoSi_(x), PtSi_(x), PdSi_(x), WSi_(x), TiSi_(x), MoSi_(x), may be used. In the description below, the gate electrode 7 n, 7 p is formed of a polycrystalline Si film by way of example. The gate electrode 7 n, 7 p may be formed of a polycrystalline SiGe (Ge concentration: 10 to 30 atomic %) film, a polycrystalline SiSn (Sn concentration: 2 to 10 atomic %) film, etc. Needless to say, the gate electrode may be a single-crystal semiconductor layer, or a metal gate. Besides, the gate electrode may be an amorphous semiconductor layer.

To start with, as shown in FIG. 2, a p-well region 2 is formed in an nMOSFET region of a p-type Si substrate 1, and an n-well region 3 is formed in a pMOSFET region which neighbors the nMOSFET region. Device isolation insulation films are buried in device isolation trenches, which are formed in the Si substrate 1, and thus device isolation regions 4 are formed around the p-well region 2 and n-well region 3 (the p-well region 2 and n-well region 3 may be formed after the device isolation regions 4 are formed). A silicon oxide film, which becomes a gate insulation film 5, is formed on the surface of the Si substrate 1.

Subsequently, as shown in FIG. 3, a polycrystalline Si film 7 with a thickness of 100 nm, which becomes gate electrodes, is formed on the gate insulation film 5. Using a photoresist film 51 as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the nMOSFET region at a concentration of 1×10²⁰ cm⁻³ or more.

Then, using a photoresist film 52 as a mask, as shown in FIG. 4, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the pMOSFET at a concentration of 1×10²⁰ cm⁻³ or more.

As shown in FIG. 5, the polycrystalline Si film 7 and gate insulation film 5 are selectively processed (patterned) by successive reactive ion etching (RIE) in the same vacuum chamber (reaction chamber). Thereby, a gate electrode 7 n for an nMOSFET, a gate insulation film 5 n lying under the gate electrode 7 n or the nMOSFET, a gate electrode 7 p for a pMOSFET and a gate insulation film 5 p lying under the gate electrode 7 p for the pMOSFET are formed.

Following the above step, the impurities which have been implanted in the steps of FIGS. 3 and 4 are diffused. The conditions for the heat treatment are explained with reference to FIG. 6. FIG. 6 is a double-logarithmic graph in which a heat treatment temperature is plotted on the abscissa and a heat treatment time is plotted on the ordinate. In this step, the heat treatment is performed so as to meet conditions in a region indicated by hatching in FIG. 6. For example, rapid thermal annealing (RTA) is conducted in a retention time of 10 seconds or less under the condition of 1100° C. or below, e.g., 1000° C. to 1050° C. Alternatively, heat treatment is conducted by spike RTA at 1000° C. to 1050° C. Thereby, the impurities, which are ion-implanted in the steps of FIGS. 3 and 4, are diffused uniformly in the entire polycrystalline Si layer, of which the gate electrode 7 n for the nMOSFET and the gate electrode 7 p for the pMOSFET are formed, so that the diffusion may reach the interface with the gate insulation films 5 n, 5 p. The region indicated by hatching in FIG. 6 is a region in a range having an upper limit expressed by the following equation (1) and a lower limit expressed by the following equation (2): t=3×10⁻¹⁵exp(49000/T)  (1) t=3×10⁻¹⁷exp(49000/T)  (2) where t is the heat treatment time, and T (K) is the heat treatment temperature expressed by an absolute temperature.

Subsequently, as shown in FIG. 7, a silicon nitride (Si₃N₄) film is deposited on the gate electrode 7 n for the nMOSFET and gate electrode 7 p for the pMOSFET by low-pressure chemical vapor deposition (LPCVD). The silicon nitride film is then etched by RIE and selectively left on side surfaces of the gate electrode 7 n and gate insulation film 5 n and on side surfaces of the gate electrode 7 p and gate insulation film 5 p. Thereby, sidewall spacers 8 n and 8 p, which are formed of the silicon nitride film, are formed, as shown in FIG. 7.

In the next fabrication step, as shown in FIG. 8, a photoresist film 53 is formed on the surface of the n-well region 3. Using the photoresist 53, gate electrode 7 n and sidewall spacers 8 n as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. By this ion implantation, the impurity ions of Group V atoms are also implanted in the gate electrode 7 n. The conditions for the ion implantation are an acceleration energy of 5 keV and a dosage of 3×10¹⁵ cm⁻². As Group V atoms to be implanted, arsenic (As) is also usable. However, in the case of using P, defects due to ion implantation can be remedied more easily by activation heat treatment, and a pn junction leakage current can be suppressed.

Next, as shown in FIG. 9, after the photoresist 53 is removed, a photoresist 54 is similarly formed on the p-well region 2. Using the photoresist 54, gate electrode 7 p and sidewall spacers 8 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. By this ion implantation, the impurity ions of Group III atoms are also implanted in the gate electrode 7 p. The conditions for the ion implantation are an acceleration energy of 2 keV and a dosage of 3×10¹⁵ cm⁻².

In the state immediately after the end of the ion implantation in steps of FIGS. 8 and 9, inactive source/drain regions 109 a, 109 b, 110 a and 110 b are formed in regions in the Si substrate 1, which neighbor the gate electrodes 7 n and 7 p and the device isolation regions 4. Then, an activation annealing process for the inactive source/drain regions 109 a, 109 b, 110 a and 110 b is performed by using a halogen lamp as a heat source. The condition for the activation annealing process is a heat treatment condition (annealing condition) in the hatched region in the double-logarithmic graph of FIG. 6 and, for example, RTA is conducted within 10 seconds at 1000° C. or spike RTA is conducted with a peak temperature set at 1000° C. By this activation annealing process, as shown in FIG. 10, source/drain regions 9 a, 9 b, 10 a and 10 b, which are apart from the gate electrodes 7 n, 7 p and are in contact with the device isolation regions 4, are formed in the Si substrate 1. By this activation annealing process, the impurities, which are doped in the gate electrode 7 n, 7 p, can be diffused to the interface with the gate insulation film 5 n, 5 p, and crystal defects occurring in the Si substrate 1 due to ion implantation can be eliminated.

Thereafter, as shown in FIG. 11, the sidewall spacers 8 n and 8 p, which are formed of silicon nitride are removed by using hot phosphoric acid.

In the next step illustrated in FIG. 12, a photoresist film 55 is formed on the pMOSFET region. Using the photoresist 55 and the gate electrode 7 n of the nMOSFET region as a mask, atoms of Group V, e.g., arsenic (As), which become n-type impurities, are ion-implanted in the surface of the p-well region 2 of the Si substrate 1. The conditions for the ion implantation are an acceleration energy of 1.5 keV and a dosage of 1×10¹⁵ cm⁻².

As shown in FIG. 13, after the photoresist 55 is removed, a photoresist film 56 is similarly formed on the surface of the p-well region 2. Using the photoresist 56 and the gate electrode 7 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. The conditions for the ion implantation are an acceleration energy of 0.3 keV and a dosage of 1×10¹⁵ cm⁻².

FIG. 14 shows the state immediately after the ion implantation. In this state, inactive shallow extension regions 111 a, 111 b, 112 a and 112 b are formed in regions in the Si substrate 1, which neighbor the gate electrodes 7 n and 7 p and the device isolation regions 4.

Subsequently, as shown in FIG. 15, a silicon oxide (SiO₂) film 13 is deposited by LPCVD at film formation temperatures of 600° C. or less.

Further, as shown in FIG. 16, a silicon nitride (Si₃N₄) film 14 is deposited on the silicon oxide (SiO₂) film 13 by LPCVD at film formation temperatures of 600° C. or less.

Following the above step, as shown in FIG. 17, using a flashtube as a heat source, an activation annealing process is performed. For the activation annealing process, the relationship between the heat treatment temperature and heat treatment time, which is indicated in the hatched region in the double-logarithmic graph of FIG. 6, is preferable. In particular, the condition of the temperature range of 1100° C. or above is preferable. In this case, the Si substrate 1 is placed on a hot plate. In the state in which the Si substrate 1 is heated (auxiliary heating) from the back side, the upper surface of the Si substrate 1 should preferably be heated by heat emitted from the flashtube light source. In this case, the temperature for the auxiliary heating of the Si substrate 1 should preferably be set in the range of about 400° C. to 900° C. If the auxiliary heating temperature is excessively low, a high light intensity is required for heating from the upper surface. As a result, the thermal stress occurring in the Si substrate increases, leading to crystal defects such as slip and dislocation. Thus, the excessively low temperature for auxiliary heating is undesirable. On the other hand, if the auxiliary heating temperature is excessively high, the impurities would diffuse and so this is also undesirable. Although the possibility is low that damage, such as slip or dislocation, occurs in the Si substrate due to auxiliary heating, the rate of temperature rise in the auxiliary heating should preferably be made as low as possible, thereby to prevent deformation of the Si substrate. For example, it is desirable that the rate of temperature rise be set at 20° C./s or less. If the rate of temperature rise is higher than this value, warpage tends to occur in the Si substrate. If flashtube light is radiated in the state in which the Si substrate warps, the Si substrate would easily be damaged. As the auxiliary heating means, the hot plate may be replaced with other heating means such as a halogen lamp which is a kind of infrared lamp. In FIG. 17, hν indicates the energy of light, wherein h is Planck's constant and ν is a wave number (1/λ, λ: wavelength of light). By the activation annealing process, shallow-junction source extension regions 11 a and 12 b and shallow-junction drain extension regions 11 b and 12 a are formed in those portions of the Si substrate 1, which neighbor the gate electrodes 7 n, 7 p and device isolation regions 4. In the description below, the source extension regions 11 a and 12 b and drain extension regions 11 b and 12 a are referred to simply as “extension region 11 a, 11 b; 12 a, 12 b”.

In a subsequently step illustrated in FIG. 18, the silicon nitride film 14 and silicon oxide film 13 are etched by RIE and selectively left on the side surfaces of the gate electrode 7 n and gate insulation film 5 n and on the side surfaces of the gate electrode 7 p and gate insulation film 5 p. Alternatively, after the silicon nitride film 14 and silicon oxide film 13 are completely removed by hot phosphoric acid and hydrofluoric acid or after the uppermost-layer silicon nitride film 14 is removed by hot phosphoric acid, a silicon nitride film and a silicon oxide film, for instance, may newly be formed and selectively left by RIE on the side surfaces of the gate electrode 7 n, 7 p and gate insulation film 5 n, 5 p. Thereby, as shown in FIG. 18, sidewall spacers having the stacked structure comprising the silicon oxide film 21 n, 21 p and silicon nitride film 22 n, 22 p or sidewall spacers having the single-layer structure comprising the silicon oxide film or silicon nitride film are formed. The thickness of the insulation film, which becomes the sidewall spacer, is set at 20 to 40 nm as the thickness of the silicon oxide film and silicon nitride film combined. The sidewall spacer functions to prevent a Ni silicide reaction in a later fabrication step, and thus the basic structure of the semiconductor device according to the first embodiment is completed.

Although the subsequent fabrication steps are not illustrated in the drawings, an Ni film is formed on the gate electrodes 7 n and 7 p and source/drain regions 9 a, 9 b, 10 a and 10 b, and Ni silicide (Ni₂Si, NiSi_(x)) layers 33 n, 33 p, 31 a, 31 b, 32 a and 32 b are formed by RTA on the upper parts of the gate electrodes 7 n and 7 p and the surfaces of the source/drain regions 9 a, 9 b, 10 a and 10 b. After the siliciding step, Ni that was not reacted in the siliciding step is removed by using sulfuric peroxide mixture (SPM), and a silicon oxide film which becomes an interlayer insulation film 24 is deposited. Contact holes are made in the interlayer insulation film 24, thereby exposing parts of the Ni silicide layers 31 a, 31 b, 32 a and 32 b on the surfaces of the source/drain regions 9 a, 9 b, 10 a and 10 b. Although not shown, on the far side of the sheet surface of FIG. 1, contact holes, which expose parts of the Ni silicide layers 33 n, 33 p on top of the gate electrode 7 n, 7 p, are also formed in the interlayer insulation film 24. Contact plugs 41 a, 41 b, 42 a and 42 b are buried in the contact holes formed in the interlayer insulation film 24. Wiring lines 43 a and 43 b for the nMOSFET are connected to the source/drain regions 9 a and 9 b of the nMOSFET via the Ni silicide layers 31 a, 31 b and contact plugs 41 a, 41 b. Wiring lines 44 a and 44 b for the pMOSFET are connected to the source/drain regions 10 a and 10 b of the pMOSFET via the Ni silicide layers 32 a, 32 b and contact plugs 42 a, 42 b.

At this time, though not shown, on the far side of the sheet surface of FIG. 1, gate wiring lines are connected to the Ni silicide layers 33 n, 33 p on top of the gate electrodes 7 n, 7 p via contact plugs buried in the contact holes which are formed in the interlayer insulation film 24.

By the above-described process, the semiconductor device with the CMOS structure, as shown in the cross section of FIG. 1, which includes the extension regions 11 a, 11 b, 12 a, 12 b each having a junction depth of 20 nm or less, is completed.

The radiation of flashtube light in the activation annealing process illustrated in FIG. 17 is, in typical cases, executed by a single light emission (1 pulse) with use of, e.g., a xenon flashtube. The light energy density of 1 pulse depends on the pulse width and the temperature of auxiliary heating of the substrate. For example, in the case of a pulse width of 1 ms, the light energy density is in the range of about 25 J/cm² to 35 J/cm² and in the range of 5 J/cm² to 15 J/cm² in relation to the auxiliary heating temperatures 400° C. and 900° C. of the Si substrate 1, respectively. If the radiation energy is too low, the activation becomes insufficient and this is undesirable. If the radiation energy is too high, the thermal stress occurring in the Si substrate increases and this is also undesirable. As regards the pulse duration time, it is desirable that the half-value width (the period in which at least ½ of the peak intensity is kept) be in the range of about 0.1 ms to 100 ms. If the pulse width is less than this value, heating is executed more instantaneously, and the thermal stress occurring in the surface portion of the Si substrate 1 would increase and this is undesirable. If the pulse width is too large, the impurities would diffuse and this is also undesirable. In the fabrication method of the semiconductor device according to the first embodiment, the activation annealing process is carried out under the condition that the substrate auxiliary heating temperature is 400° C. and the radiation energy density is 28 J/cm².

The xenon flashtube light, which is radiated from above the surface of the Si substrate 1, passes through the insulation film comprising the silicon oxide film 13 and silicon nitride film 14 and is absorbed by the gate electrodes 7 n and 7 p and the extension regions 111 a, 111 b, 112 a and 112 b and the source/drain regions 9 a, 9 b, 10 a and 10 b in the Si substrate 1. The temperature rises in the gate electrodes 7 n and 7 p, the extension regions 111 a, 111 b, 112 a and 112 b and the source/drain regions 9 a, 9 b, 10 a and 10 b, which have absorbed the xenon flashtube light. It is considered that the temperature of the gate electrodes 7 n and 7 p, the extension regions 111 a, 111 b, 112 a and 112 b and the source/drain regions 9 a, 9 b, 10 a and 10 b instantaneously exceeds 1200° C. By this temperature, the impurities, which are doped in the gate electrodes 7 n and 7 p, the extension regions 111 a, 111 b, 112 a and 112 b and the source/drain regions 9 a, 9 b, 10 a and 10 b, are electrically activated.

The resistance in the gate electrodes 7 n and 7 p, the extension regions 111 a, 111 b, 112 a and 112 b and the source/drain regions 9 a, 9 b, 10 a and 10 b is decreased by the activation annealing process illustrated in FIG. 17. The annealing using the lash lamp is carried out via the silicon oxide film 13 and silicon nitride film 14, and thus the difference in refractive index between the atmospheric layer and the Si substrate 1 can be decreased. By adjusting the thicknesses of the respective insulation films, the reflectance at the interface of the Si substrate can be reduced. Thereby, the reflectance which varies depending on dense/non-dense parts of patterns can be made uniform, and the dependency on patterns can be eliminated. Moreover, since both the silicon oxide film and silicon nitride film are optically transparent films, the heating efficiency is not lowered. By the degree corresponding to the decrease in reflectance, the heating temperature can be increased with less radiation energy.

EXPERIMENTAL COMPARISON

[Gate Leakage Current]

As regards the nMOSFET according to the first embodiment, after the nMOSFET was completed, gate leakage current was measured by providing wiring as shown in FIG. 19. FIG. 19 shows a cross section of the nMOSFET according to the present embodiment and a measuring circuit for measuring a gate leakage current of the nMOSFET. FIG. 20 is a plan view of the gate electrode 7 n of the nMOSFET shown in FIG. 19. FIG. 21 is a characteristic graph in which the structure of the first embodiment and the structures of a first comparative example (comparative example 1-1) and a second comparative example (comparative example 1-2) are compared with respect to in-plane variations of gate leakage currents in nMOSFETs. In FIG. 21, the ordinate indicates a cumulative distribution ln(−ln(1−F)) according to Weibull distribution, and the abscissa indicates a gate leakage current. In this comparison, in the structure according to the first embodiment, an nMOSFET with a gate length of 30 nm was fabricated under the condition that arsenic (As) is doped in the ion-implantation step of FIG. 3 with an acceleration energy of 20 keV and a dosage of 5×10¹⁵ cm⁻². On the other hand, in the first comparative example (comparative example 1-1), an nMOSFET with a gate length of 30 nm was fabricated under the condition that phosphorus (P) is doped in the ion-implantation step of FIG. 3 with an acceleration energy of 5 keV and a dosage of 5×10¹⁵ cm⁻². In the second comparative example (comparative example 1-2), an nMOSFET with a gate length of 30 nm was fabricated under the condition that phosphorus (P) is doped in the ion-implantation step of FIG. 3 with an acceleration energy of 5 keV and a dosage of 5×10¹⁵ cm⁻², following which a spike RTA process, instead of flashtube annealing, is carried out at 1030° C. in the activation annealing step of FIG. 17 with use of a conventional halogen lamp.

As shown in FIG. 21, in the first embodiment, as in the second comparative example (comparative example 1-2) in which the flashtube is not used, the value of gate leakage current was low in all chips in the plane, and there was no defective chip. In the first comparative example (comparative example 1-1), however, it was confirmed that the gate leakage current increased by one to three orders of magnitude and the gate withstand voltage greatly deteriorated.

[Junction Depth of Extension Region]

FIG. 22 is a graph showing the relationship between the depth from the surface of the silicon substrate and the impurity concentration in the structure according to the present embodiment and the structure according to the second comparative example (comparative example 1-2). In this graph, the impurity profile in the extension region 11 a, 11 b, 12 a, 12 b was measured by secondary ion mass spectrometry (SIMS).

As shown in FIG. 22, in the first embodiment, the depth of the diffusion layer was kept at 20 nm or less, and a steep impurity profile was obtained. By contrast, in the second comparative example (comparative example 1-2), the impurities were diffused to a great degree.

As is understood from the above result, in the first comparative example (comparative example 1-1), the gate withstand voltage deteriorates, and it is difficult to fabricate a transistor with a fine structure. In the second comparative example (comparative example 1-2), no deterioration is observed in gate withstand voltage, but a shallow diffusion layer cannot be formed. It is thus understood that a transistor with a fine structure cannot be fabricated. Further, it was confirmed by SIMS and C-V measurement that in the first embodiment, arsenic (As) with a lower diffusion coefficient than phosphorus (P) is used as a dopant, but the dopant is sufficiently diffused in the gate polycrystalline Si in the subsequent RTA process. In short, the gate current is not suppressed because the apparent thickness of the gate insulation film increases due to gate depletion.

<Theoretical Comparison>

In the first comparative example (comparative example 1-1), the dosage of P in the gate electrode 7 n that is formed of polycrystalline Si, as combined with the dosage at the time of formation of the source/drain regions 9 a and 9 b, is 8×10¹⁵ cm⁻². The thickness of the gate electrode 7 n is 100 nm, and since P is uniformly diffused by the heat treatment, the impurity density of P reaches as high as 8×10²⁰ cm⁻³. Further, in the first comparative example (comparative example 1-1), flashtube annealing is performed as final activation annealing. In the very rapid annealing by flashtube annealing or laser annealing, the instantaneous maximum temperature of the surface of the Si substrate 1 reaches as high as 1200° C. to 1300° C. Since the thickness of the single-crystal Si substrate 1 is as great as 730 μm, the heat that is absorbed by the source/drain region 9 a, 9 b diffuses to the deep part of the Si substrate. However, since the gate electrode 7 n is formed on the insulation film, the heat does not easily escape from the gate electrode 7 n. It is considered that since the heat concentrates in the gate electrode 7 n with the thickness of 100 nm, the temperature of the gate electrode 7 n rises up to about 1300° C. to 1400° C.

In other words, despite the radiation being performed with the same optical energy, the temperature of the gate electrode 7 n is higher than that of the Si substrate 1. Phosphorus (P), which is doped in the abnormally heated gate electrode 7 n that is formed of polycrystalline Si, diffuses and piles up at the interface of the gate insulation film. The phosphorus (P), the concentration of which is further increased at the interface, permeates into the gate insulation film 5 n and stays in the gate insulation film 5 n, thus locally forming phosphorus silicate glass (PSG). It is considered that the gate insulation film 5 n is fluidized due to the drop in melting point, which results from the formation of PSG, and a leakage path is formed. Similarly, in the second comparative example (comparative example 1-2), the impurity density of P in the gate electrode 7 n reaches as high as 8×10²⁰ cm⁻³. However, since the conventional RTA is performed, abnormal heating up to 1300° C. or more does not occur in the gate electrode 7 n that is formed of polycrystalline Si. Hence, even if the impurity density. of P is high, the gate leakage current does not increase. On the other hand, in the first embodiment, arsenic (As) is doped at 5×10¹⁵ cm⁻² prior to the processing of the gate, and P is doped at 3×10¹⁵ cm⁻² at the time of forming the source/drain regions 9 a, 9 b, and the maximum concentration of P is 3×10²⁰ cm⁻³ at most. It is thus considered that even if the activation process is performed by flashtube annealing, the PSG does not easily form since the diffusion efficiency of As is lower than that of P and the impurity density of P that permeates into the gate insulation film 5 n is low even if P piles up at the interface of the gate insulation film 5 n.

FIG. 23 shows, with attention paid to the nMOSFET, the relationship between the impurity density of As and the impurity density of P in the gate electrode 7 n formed of polycrystalline Si and the gate leakage current in the case where the flashtube annealing is applied. As shown in FIG. 23, simply by reducing the impurity density of P, most of P is trapped in lattice positions of Si and contributes to activation, and the amount of excess P that is not used for activation is decreased. It is thus considered that P does not easily pile up at the interface of the insulation film. However, if the concentration of the dopant in the polycrystalline Si is too low, the activation density decreases and gate depletion occurs. As a result, the driving power of the transistor is not enhanced. It is necessary to secure the activation density of at least 1×10²⁰ cm⁻³ or more.

FIG. 24 shows the relationship between the gate leakage current and the diffusion layer sheet resistance due to P and As (acceleration energy: 1.5 keV; dosage: 1×10¹⁵ cm⁻²) doped in the shallow-junction extension region 11 a, 11 b, in the case where P is used and in the case where As is used as the dopant in the gate electrode 7 n that is formed of polycrystalline Si. As shown in FIG. 24, it is understood that even in the case where the impurity density is the same, the use of As, compared to the use of P, can more reduce the sheet resistance of the extension region 11 a, 11 b within such a range as not to increase the gate leakage current. In other words, it is understood that the use of As can more suppress the gate leakage current even if the radiation optical energy is increased at the time of flashtube annealing, and the process window relating to the heat treatment process is increased.

(First Modification of First Embodiment)

Next, a description is given of a first modification of the first embodiment with attention paid to the nMOSFET, in which the nMOSFET is fabricated under the following conditions. In the ion-implantation step of FIG. 3, P is doped with an acceleration energy of 5 keV and a dosage of 5×10¹⁵ cm⁻². In addition, the activation annealing process step of FIG. 17 is carried out under the flashtube annealing condition that the auxiliary heating temperature of the Si substrate 1 is 750° C. and the radiation energy density is 18 J/cm².

The above-described first comparative example (comparative example 1-1) and the first modification of the first embodiment are different with respect to the flashtube annealing condition. In the first modification of the first embodiment, the auxiliary heating temperature of the Si substrate 1 is higher but the radiation energy density is lower. However, the sheet resistance of the extension region 11 a, 11 b is 730 Ω/sq (sq: unit area (square)) in the first comparative example (comparative example 1-1), while this sheet resistance is 610 Ω/sq in the first modification of the first embodiment and is low. In other words, it is understood that the temperature is higher in the first modification of the first embodiment than in the first comparative example (comparative example 1-1). Despite this, it is understood that in the first modification of the first embodiment the gate leakage current is successfully suppressed to the same degree as in the first embodiment.

FIG. 25 is a graph showing the relationship between the sheet resistance and gate leakage current, with the auxiliary heating temperature of the silicon substrate being used as a parameter. FIG. 25 indicates the dependence of the gate leakage current and the sheet resistance of the extension region 11 a, 11 b upon the auxiliary heating of the Si substrate 1. From FIG. 25, it is understood that although the impurity density of P in the gate electrode 7 n that is formed of polycrystalline Si is unchanged, the sheet resistance of the extension region 11 a, 11 b can be reduced within such a range as not to increase the gate leakage current if the auxiliary heating temperature of the Si substrate 1 is raised. It is understood that the process window relating to the heat treatment step, as a result, is increased. It is considered that the result shown in FIG. 25 was obtained because in the first modification of the first embodiment the high-concentration activation of the diffusion layer was realized with a radiation energy which is less by a degree corresponding to the increase in auxiliary heating temperature of the Si substrate 1. It is also considered that since the contribution of very rapid flashtube heating is decreased, the abnormal high heating of polycrystalline Si can be suppressed and PSG is not easily formed due to permeation of P into the gate insulation film 5 n.

As has been described in connection with the first embodiment and the first modification of the first embodiment with attention paid to the nMOSFET, both the reduction in diffusion layer sheet resistance and the suppression of gate leakage current can be realized by decreasing the impurity density of P in the gate electrode 7 n that is formed of polycrystalline Si, or by forming the gate electrode that is formed of polycrystalline Si including As as a main component. In short, according to the semiconductor device fabrication methods of the first embodiment and the first modification, the activation process of the extension region 11 a, 11 b with a wide process window relating to the heat treatment step can be realized, and nMOSFETs with fine structures can easily be fabricated.

In the above descriptions of the semiconductor device and fabrication method, attention has been paid to the nMOSFET. Needless to say, the same advantageous effects can be obtained by applying the same techniques to the pMOSFET.

(Second Modification of First Embodiment)

In the methods for fabricating the semiconductor devices according to the first embodiment and the first modification thereof, the annealing device was described as employing the xenon flashtube as the light source for light radiation. However, the semiconductor device fabrication method is not limited to this example, and the light source may be, for instance, any one of flashtubes using other rare gases, mercury and hydrogen, an arc discharge lamp, an excimer laser, an Ar laser, an N2 laser, a YAG laser, a titanium-sapphire laser, a CO laser, and a CO₂ laser.

In the above-described methods, the shallow-junction extension regions 11 a and 11 b are formed after the deep-junction source/drain regions 9 a and 9 b are formed. However, as shown in FIGS. 26 to 33, the shallow-junction extension regions 11 a and 11 b may first be formed, following which the deep-junction source/drain regions 9 a and 9 b may be formed.

This fabrication method will now be described with reference to FIGS. 26 to 33. FIGS. 26 to 33 are cross-sectional views successively illustrating fabrication steps of a semiconductor device according to a second modification of the first embodiment. In this second modification, the fabrication steps of FIGS. 2 to 5, which have been described in connection with the semiconductor device fabrication method of the first embodiment, are similarly applied.

In the present modification, following the step of FIG. 5, a photoresist film 57 is formed on the pMOSFET region, as shown in FIG. 26, without forming sidewall spacers 8 n and 8 p. Using the photoresist 57 and gate electrode 7 n as a mask, atoms of Group V, e.g., arsenic (As), which become n-type impurities, are ion-implanted in the surface of the p-well region 2 on the surface of the Si substrate 1. The conditions for the ion implantation are, as in the first embodiment, an acceleration energy of 1.5 keV and a dosage of 1×10¹⁵ cm⁻².

Next, as shown in FIG. 27, after the photoresist 57 is removed, a photoresist 58 is similarly formed on the p-well region 2. Using the photoresist 58 and gate electrode 7 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. The conditions for the ion implantation are, as in the first embodiment, an acceleration energy of 0.3 keV and a dosage of 1×10¹⁵ cm⁻². In the state immediately after the end of this fabrication step, inactive shallow extension regions 111 a, 111 b, 112 a and 112 b are formed in regions in the Si substrate 1, which neighbor the gate electrodes 7 n and 7 p and the device isolation regions 4.

Subsequently, as shown in FIG. 28, a silicon oxide (SiO₂) film 15 is deposited by LPCVD at film formation temperatures of 600° C. or less. Further, as shown in FIG. 28, a silicon nitride (Si₃N₄) film 16 is deposited on the silicon oxide (SiO₂) film 15 by LPCVD at film formation temperatures of 600° C. or less.

Following the above step, as shown in FIG. 29, using a flashtube as a heat source, an activation annealing process is performed under the heat treatment condition indicated in the hatched region in the double-logarithmic graph of FIG. 6 (in particular, the condition of the temperature range of 1100° C. or above is preferable). In this activation annealing process, the Si substrate 1 is placed on a hot plate. In the state in which the Si substrate 1 is heated (auxiliary heating) from the back side, the upper surface of the Si substrate 1 is heated by heat emitted from the flashtube light source. In this case, the temperature for the auxiliary heating of the Si substrate 1 should preferably be set in the range of about 400° C. to 900° C. This step is the same as the step of FIG. 17, which has been described in connection with the first embodiment. By this step, shallow extension regions 11 a, 11 b, 12 a and 12 b are formed in regions in the Si substrate 1, which neighbor the gate electrodes 7 n and 7 p and the device isolation regions 4.

In a subsequently step illustrated in FIG. 30, the silicon nitride film 16 and silicon oxide film 15 are etched by RIE and selectively left on the side surfaces of the gate electrode 7 n and gate insulation film 5 n and on the side surfaces of the gate electrode 7 p and gate insulation film 5 p. Alternatively, after the silicon nitride film 16 and silicon oxide film 15 are completely removed by hot phosphoric acid and hydrofluoric acid or after the uppermost-layer silicon nitride film 16 is removed by hot phosphoric acid, a silicon nitride film and a silicon oxide film, for instance, may newly be formed and selectively left by RIE on the side surfaces of the gate electrode 7 n, 7 p and gate insulation film 5 n, 5 p. Thereby, as shown in FIG. 30, sidewall spacers having the stacked structure comprising silicon oxide film 23 n, 23 p and silicon nitride film 24 n, 24 p are formed on the side surfaces of the gate electrode 7 n and gate insulation film 5 n and on the side surfaces of the gate electrode 7 p and gate insulation film 5 p.

In the next step illustrated in FIG. 31, a photoresist film 59 is formed on the surface of the n-well region 3. Using the photoresist 59, gate electrode 7 n and sidewall spacers 23 n and 24 n as a mask, atoms of Group V, e.g., phosphorus (P) ions, which become n-type impurities, are ion-implanted in the surface of the p-well region 2. By this ion implantation, the impurity ions of Group V atoms are also implanted in the gate electrode 7 n. The conditions for the ion implantation are, as in the first embodiment, an acceleration energy of 5 keV and a dosage of 3×10¹⁵ cm⁻². As Group V atoms to be implanted, arsenic (As) is also usable. However, in the case of using P, defects due to ion implantation can be remedied more easily by activation heat treatment, and a pn junction leakage current can be suppressed. After the photoresist 59 is removed, a photoresist 60 is similarly formed on the p-well region 2. Using the photoresist 60, gate electrode 7 p and sidewall spacers 23 p and 24 p as a mask, atoms of Group III, e.g., boron (B) ions, which become p-type impurities, are ion-implanted in the surface of the n-well region 3, as shown in FIG. 32. By this ion implantation, the impurity ions of Group III atoms are also doped in the gate electrode 7 p. The conditions for the ion implantation are an acceleration energy of 2 keV and a dosage of 3×10¹⁵ cm⁻², as in the semiconductor device fabrication method according to the first embodiment. In the state immediately after the end of this fabrication step, inactive source/drain regions 109 a, 109 b, 110 a and 110 b are formed in regions in the Si substrate 1, which neighbor the gate electrodes 7 n and 7 p and the device isolation regions 4.

Subsequently, as shown in FIG. 33, a silicon oxide (SiO₂) film 17 is deposited by LPCVD at film formation temperatures of 600° C. or less. Further, a silicon nitride (Si₃N₄) film 18 is deposited the silicon oxide (SiO₂) film 17 by LPCVD at film formation temperatures of 600° C. or less. Using a halogen lamp as a heat source, an activation annealing process for the Si substrate 1 is carried out. The condition for the activation annealing process is a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6 and, for example, RTA is conducted within 10 seconds at 1000° C. or spike RTA is conducted with a peak temperature set at 1000° C. By this activation annealing process, source/drain regions 9 a, 9 b, 10 a and 10 b, which are apart from the gate electrodes 7 n, 7 p and are in contact with the device isolation regions 4, are formed in the Si substrate 1. By this activation annealing process, the impurities, which are doped in the gate electrode 7 n, 7 p, can be diffused to the interface with the gate insulation film 5 n, 5 p, and crystal defects occurring in the Si substrate 1 due to ion implantation can be eliminated.

Thereafter, the sidewall spacers 23 n, 24 n, 23 p and 24 p are left so as to function to prevent a Ni silicide reaction in a later fabrication step. Thus, the basic structure of the semiconductor device according to the present modification is completed. The fabrication steps following the step of FIG. 33 are the same as those in the semiconductor device fabrication method according to the first embodiment, so a description thereof is omitted here. By the above-described semiconductor device fabrication method according to the second embodiment of the first embodiment, too, the semiconductor device with the CMOS structure, as shown in the cross section of FIG. 1, which includes the extension regions 11 a, 11 b, 12 a and 12 b each having a junction depth of 20 nm or less, can be completed.

(Second Embodiment)

Next, a semiconductor device and a method for fabricating the semiconductor device, according to a second embodiment of the invention, are described. In the second embodiment, as in the description of the first embodiment, a first conductivity type and a second conductivity type are mutually opposite conductivity types. In the description of the second embodiment and a modification thereof, it is assumed that the first conductivity type is p-type and the second conductivity type is n-type. Alternatively, the first conductivity type may be n-type and the second conductivity type may be p-type. FIG. 34 is a cross-sectional view of a semiconductor device according to the second embodiment of the invention.

As shown in FIG. 34, the semiconductor device according to the second embodiment, as in the first embodiment, has a CMOS structure. In the second embodiment, offset spacers 6 n and 6 p, which are formed of silicon oxide films, are newly provided in the structure that has been described with reference to FIG. 1 in connection with the first embodiment.

The offset spacers 6 n are formed on side walls of the gate electrode 7 n and gate insulation film 5 n of the nMOSFET. Specifically, in the structure shown in FIG. 1, each offset spacer 6 n is newly formed between the gate electrode 7 n and gate insulation film 5 n, on the one hand, and the sidewall spacer 21 n, on the other hand.

The offset spacers 6 p are formed on side walls of the gate electrode 7 p and gate insulation film 5 p of the pMOSFET. Specifically, in the structure shown in FIG. 1, each offset spacer 6 p is newly formed between the gate electrode 7 p and gate insulation film 5 p, on the one hand, and the sidewall spacer 21 p, on the other hand.

The surface concentration of the extension region 11 a, 11 b of the nMOSFET is set at an impurity density of about 5×10¹⁹ cm⁻³ to 1×10²¹ cm⁻³, preferably at an impurity density of about 1×10²⁰ cm⁻³ to 8×10²⁰ cm⁻³. The junction depth of the extension region 11 a, 11 b of the nMOSFET is set at 20 nm or less. The surface concentration of the extension region 12 a, 12 b of the pMOSFET is set at an impurity density of about 5×10¹⁹ cm⁻³ to 1×10²¹ cm⁻³, preferably at an impurity density of about 1×10²⁰ cm⁻³ to 8×10²⁰ cm⁻³. The junction depth of the extension region 12 a, 12 b of the pMOSFET is also set at 20 nm or less.

In the other structural aspects, the second embodiment is the same as the first embodiment. FIG. 35 is an enlarged cross-sectional view of a part of the nMOSFET in which the offset spacer 6 n is not provided, and FIG. 36 is an enlarged cross-sectional view of a part of the nMOSFET according to the present embodiment.

As is shown in FIG. 36, the offset spacer 6 n, which is provided on the right side of the gate electrode 7 n, has the function that is to be described below. A gate offset region with a dimension of Δd in the gate length direction is provided between an end portion of the extension region 11 b and the gate electrode 7 n in the structure shown in FIG. 35. This gate offset region functions to reduce an overlap capacitance Cov between the gate electrode 7 n and the extension region 11 b.

Although not shown, the offset spacer 6 n, which is provided on the left side of the gate electrode 7 n, similarly forms a gate offset region with a dimension of Δd between an end portion of the extension region 11 a and the gate electrode 7 n. Thereby, this gate offset region functions to reduce an overlap capacitance Cov between the gate electrode 7 n and the extension region 11 a. By choosing the film thickness Δd of the offset spacer 6 n in the range of about 1 to 10 nm, the gate overlap capacitance Cov per unit gate width can be set at about 1×10⁻¹⁵ F/μm to 1×10⁻¹⁶ F/μm. Representatively, the film thickness Δd of about 4 nm can be adopted.

The above description with reference to FIGS. 35 and 36 is also applicable to the pMOSFET. Specifically, by providing the offset spacers 6 p on the side walls of the gate electrode 7 p, the gate overlap capacitance Cov per unit gate width of the pMOSFET can be set at about 1×10⁻¹⁵ F/μm to 1×10⁻¹⁶ F/μm. Typically, the film thickness of the offset spacer 6 p can be set at, e.g., about 4 nm.

Next, a method for fabricating the semiconductor device according to the present embodiment is described with reference to FIGS. 37 to 47. FIGS. 37 to 47 are cross-sectional views successively illustrating fabrication steps of the semiconductor device shown in FIG. 34. The semiconductor device fabrication method to be described below is merely an example, and the semiconductor device of this embodiment may, needless to say, be fabricated by other various methods including modifications of the method described below. For example, in the description below, the gate electrodes 7 n, 7 p are formed of polycrystalline Si films. However, this is merely an example, and the gate electrodes 7 n, 7 p may be formed of, e.g., polycrystalline SiGe (Ge concentration: 10 to 30 atomic %), a single-crystal semiconductor layer, or a metal layer.

To start with, the fabrication steps of FIGS. 2 to 5, as described in connection with the first embodiment, are carried out. In the first embodiment, immediately after the step of FIG. 5, sidewall spacers 8 n, 8 p are formed of silicon nitride films, as shown in FIG. 7. However, in the second embodiment, prior to the formation of the sidewall spacers 8 n, 8 p, a silicon oxide (SiO₂) film is deposited by LPCVD at film formation temperatures of 600° C. or less within the range of film thickness of about 2 to 10 nm, for example, with a film thickness of 4 nm. The silicon oxide film is etched by a method of leaving sidewall parts thereof using RIE, and thus the silicon oxide film is selectively left on the side surfaces of the gate electrode 7 n, 7 p and gate insulation film 5 n, 5 p. As a result, offset spacers 6 n, 6 p, as shown in FIG. 37, which are formed of silicon oxide films, are completed. The offset spacer 6 n, 6 p provides a gate offset region between an end portion of the impurity diffusion region formed in the Si substrate (to be described later) and the gate electrode. The film thickness of the offset spacer 6 n, 6 p determines the degree of reduction in overlap capacitance Cov with the gate electrode.

Subsequently, fabrication steps similar to those of FIGS. 7 to 18, which have been described in connection with the first embodiment, are performed. Specifically, as shown in FIG. 38, a silicon nitride (Si₃N₄) film is deposited by LPCVD at 600° C. or less, and selectively left on side surfaces of the offset spacers 6 n, 6 p. Thereby, sidewall spacers 8 n and 8 p are formed. Alternatively, the offset spacers 6 n, 6 p may be formed of silicon nitride films, and the sidewall spacers 8 n, 8 p may be formed of silicon oxide films.

In the next fabrication step, as shown in FIG. 39, a photoresist film 61 is formed on the surface of the n-well region 3. Using the gate electrode 7 n, offset spacers 6 n, sidewall spacers 8 n and photoresist 61 as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. At this time, the ions of Group V atoms are also implanted in the gate electrode 7 n. The conditions for the ion implantation are an acceleration energy of 5 keV and a dosage of 3×10¹⁵ cm⁻². As Group V atoms to be implanted, arsenic (As) is also usable. However, in the case of using P, defects due to ion implantation can be remedied more easily by activation heat treatment, and a pn junction leakage current can be suppressed.

Next, as shown in FIG. 40, a photoresist 62 is formed on the surface of the p-well region 2. Using the gate electrode 7 p, offset spacers 6 p, sidewall spacers 8 p and photoresist 62 as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ionized and implanted in the surface of the n-well region 3, as shown in FIG. 40. At this time, the impurity ions of Group III atoms are also implanted in the gate electrode 7 p. The conditions for the ion implantation are an acceleration energy of 2 keV and a dosage of 3×10¹⁵ cm⁻².

In the state immediately after the end of the ion implantation in steps of FIGS. 39 and 40, inactive source/drain regions 109 a, 109 b, 110 a and 110 b are formed in regions in the Si substrate 1, which neighbor the offset spacers 6 n and 6 p and the device isolation regions 4. Then, an activation annealing process for the inactive source/drain regions 109 a, 109 b, 110 a and 110 b is performed by using a halogen lamp as a heat source. The condition for the activation annealing process is a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6 and, for example, RTA is conducted within 10 seconds at 1000° C. to 1050° C. or spike RTA is conducted with a peak temperature set at 1000° C. to 1050° C. This step corresponds to the step of FIG. 10 which has been described in connection with the first embodiment. By this activation annealing process, as shown in FIG. 41, source/drain regions 9 a, 9 b, 10 a and 10 b, which are apart from end portions of the gate electrodes 7 n, 7 p and are in contact with the device isolation regions 4, are formed in the Si substrate 1. By this activation annealing process, the impurities, which are doped in the gate electrode 7 n, 7 p, can be diffused to the interface with the gate insulation film 5 n, 5 p, and crystal defects occurring in the Si substrate 1 due to ion implantation can be eliminated.

Thereafter, as shown in FIG. 42, the sidewall spacers 8 n and 8 p, which are formed of silicon nitride, are removed by using hot phosphoric acid.

In the next step illustrated in FIG. 43, a photoresist film 63 is formed on the pMOSFET region. Using the gate electrode 7 n, offset spacers 6 n and photoresist 63 of the nMOSFET region as a mask, atoms of Group V, e.g., arsenic (As), which become n-type impurities, are ion-implanted in the surface of the p-well region 2 on the surface of the Si substrate 1. The conditions for the ion implantation are an acceleration energy of 5 keV and a dosage of 2×10¹⁴ cm⁻².

As shown in FIG. 44, after the photoresist 63 is removed, a photoresist film 64 is similarly formed on the surface of the p-well region 2. Using the gate electrode 7 p, offset spacers 6 p and photoresist 64 as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. The conditions for the ion implantation are an acceleration energy of 0.9 keV and a dosage of 2×10¹⁴ cm⁻². In the state shown in FIG. 44, inactive shallow extension regions 111 a, 111 b, 112 a and 112 b are formed in regions of the Si substrate 1, which neighbor the gate electrodes 7 n, 7 p and device isolation regions 4.

Subsequently, as shown in FIG. 45, a silicon oxide (SiO₂) film 13 is deposited by LPCVD at film formation temperatures of 600° C. or less, and then a silicon nitride (Si₃N₄) film 14 is deposited on the silicon oxide (SiO₂) film 13 by LPCVD at film formation temperatures of 600° C. or less.

Following the above step, as shown in FIG. 46, using a flashtube as a heat source, an activation annealing process is performed. This step is the same as the step of FIG. 17 which has been described in connection with the first embodiment. The activation annealing process is performed under the heat treatment condition indicated in the hatched region in the double-logarithmic graph of FIG. 6. By the activation annealing process, shallow extension regions 11 a, 11 b, 12 a and 12 b, as shown in FIG. 46, are formed in those portions of the Si substrate 1, which neighbor the offset spacers 6 n and 6 p and device isolation regions 4.

In a subsequently step illustrated in FIG. 47, the silicon nitride film 14 and silicon oxide film 13 are etched by RIE and selectively left on the side surfaces of the offset spacers 6 n, 6 p. Alternatively, after the silicon nitride film 14 and silicon oxide film 13 are completely removed by hot phosphoric acid and hydrofluoric acid or after the uppermost-layer silicon nitride film 14 is removed by hot phosphoric acid, a silicon nitride film and a silicon oxide film, for instance, may newly be formed and selectively left by RIE on the side surfaces of the offset spacers 6 n, 6 p. Thereby, sidewall spacers having the stacked structure comprising the silicon oxide film 21 n, 21 p and silicon nitride film 22 n, 22 p or sidewall spacers having the single-layer structure comprising the silicon oxide film or silicon nitride film are formed. The thickness of the insulation film excluding the offset spacer 6 n, 6 p, which finally becomes the sidewall spacer, is set at 20 to 40 nm as the thickness of the silicon oxide film 21 n, 21 p and silicon nitride film 22 n, 22 p combined. The sidewall spacer functions to prevent a Ni silicide reaction in a later fabrication step, and thus the basic structure of the semiconductor device according to the second embodiment is completed.

The subsequent fabrication steps are the same as those in the first embodiment, so a description thereof is omitted here. By the above-described process, the semiconductor device with the CMOS structure, as shown in the cross section of FIG. 34, which includes the extension regions 11 a, 11 b, 12 a, 12 b each having a junction depth of 20 nm or less, is completed.

The radiation of flashtube light in the activation annealing process illustrated in FIG. 46 is, in typical cases, executed by a single light emission (1 pulse) with use of, e.g., a xenon flashtube. This annealing process is the same as the step described with reference to FIG. 17 in connection with the first embodiment. Specifically, the light energy density of 1 pulse depends on the pulse width and the temperature of auxiliary heating of the substrate. For example, in the case of a pulse width of 1 ms, the light energy density is in the range of about 25 J/cm² to 35 J/cm² and in the range of 5 J/cm² to 15 J/cm² in relation to the auxiliary heating temperatures of 400° C. and 900° C. of the Si substrate 1, respectively. Thereby, the impurities, which are doped in the gate electrodes 7 n and 7 p, the extension regions 111 a, 111 b, 112 a and 112 b and the source/drain regions 9 a, 9 b, 10 a and 10 b, are electrically activated. By the activation, the resistance in the gate electrodes 7 n and 7 p, the extension regions 11 a, 11 b, 12 a and 12 b and the source/drain regions 9 a, 9 b, 10 a and 10 b is decreased. The annealing using the lash lamp is carried out via the silicon oxide film 13 and silicon nitride film 14, and thus the difference in refractive index between the atmospheric layer and the Si substrate 1 can be decreased. By adjusting the thicknesses of the respective insulation films, the reflectance at the interface of the Si substrate 1 can be reduced.

Experimental Comparison

[Gate Leakage Current]

FIG. 48 is a graph in which the semiconductor device fabrication method according to the second embodiment is compared with a first comparative example (comparative example 2-1) and a second comparative example (comparative example 2-2) with respect to in-plane variations of gate leakage currents in nMOSFETs. In FIG. 48, the ordinate indicates a cumulative distribution ln(−ln(1−F)) according to Weibull distribution, and the abscissa indicates a gate leakage current. The gate leakage current is measured by using the wiring shown in FIG. 19, which has been described in connection with the first embodiment. Symbol F in the Weibull distribution is a cumulative failure rate which is expressed by F(t)=1−exp(−(t/η)^(m)), where t is time, m is a Weibull coefficient, and η is a scale parameter.

The semiconductor according to this embodiment was fabricated under the following conditions. Specifically, in the offset spacer formation step of FIG. 37, the offset spacer 6 n, 6 p was formed with a thickness of 6 nm. In addition, arsenic (As) was doped in the ion-implantation step of FIG. 43 with an acceleration energy of 5 keV and a dosage of 2×10¹⁴ cm⁻², and boron (B) was doped in the ion-implantation step of FIG. 44 with an acceleration energy of 0.9 keV and a dosage of 2×10¹⁴ cm⁻². Thereby, an nMOSFET with a gate length of 30 nm was fabricated.

An nMOSFET according to the first comparative example (comparative example 2-1) was fabricated under the conditions that no offset spacer 6 n, 6 p was provided in the offset spacer formation step of FIG. 37, and arsenic (As) was doped in the ion-implantation step of FIG. 43 with an acceleration energy of 2 keV and a dosage of 1×10¹⁵ cm⁻², and boron (B) was doped in the ion-implantation step of FIG. 44 with an acceleration energy of 0.3 keV and a dosage of 1×10¹⁵ cm⁻². Thus, an nMOSFET with a gate length of 30 nm was fabricated.

An nMOSFET according to the second comparative example (comparative example 2-2) was fabricated under the following conditions. Specifically, no offset spacer 6 n, 6 p was provided in the offset spacer formation step of FIG. 37, and arsenic (As) was doped in the ion-implantation step of FIG. 43 with an acceleration energy of 2 keV and a dosage of 1×10¹⁵ cm⁻², and boron (B) was doped in the ion-implantation step of FIG. 44 with an acceleration energy of 0.3 keV and a dosage of 1×10¹⁵ cm⁻². Then, a spike RTA process, instead of flashtube annealing, was carried out at 1030° C. in the step of FIG. 46 with use of a conventional halogen lamp. Thereby, an nMOSFET with a gate length of 30 nm was fabricated.

As shown in FIG. 48, in the nMOSFET according to the present embodiment, as in the second comparative example (comparative example 2-2) in which the flashtube is not used, the value of gate leakage current was low in all chips in the plane, and there was no defective chip. In the comparative example 2-1, compared to the present embodiment, however, it was confirmed that the gate leakage current increased by one to three orders of magnitude and the gate withstand voltage greatly deteriorated.

[Junction Depth of Extension Region]

FIG. 49 is a graph showing the relationship between the depth from the surface of the silicon substrate and the impurity concentration in the structure according to the present embodiment and the structures according to the first and second comparative examples. In this graph, the impurity profile in the extension region 11 a, 11 b of the nMOSFET was measured by secondary ion mass spectrometry (SIMS).

As shown in FIG. 49, in each case, the sheet resistance is suppressed to 700 Ω/sq. In the nMOSFETs according to the second embodiment and comparative example 2-1, the depth of the diffusion layer was kept at 20 nm or less, and a shallow impurity density profile was obtained. However, in the comparative example 2-2, the impurities were diffused to a deep region of the substrate.

As is understood from the above result, in the nMOSFET according to the comparative example 2-1, the gate withstand voltage deteriorates, and the characteristics of this nMOSFET are improper as those of an nMOSFET to be obtained. On the other hand, in the nMOSFET according to the comparative example 2-2, no deterioration is observed in gate withstand voltage, but a shallow diffusion layer cannot be formed. It is thus difficult to fabricate a transistor with a fine structure.

<Theoretical Comparison>

In the nMOSFET according to the comparative example 2-1, the impurity density in the substrate surface of the extension region 11 a, 11 b becomes 1×10²¹ cm⁻³ or more. In addition, as shown in FIG. 35, the end portion of the extension region 11 a, 11 b overlaps with the gate electrode 7 n, and the overlap capacitance Cov is as high as 2×10⁻¹⁶ F/μ m. Further, in the nMOSFET according to the comparative example 2-1, flashtube annealing is performed as final activation annealing. In the very rapid annealing by flashtube annealing or laser annealing, the instantaneous maximum temperature of the surface of the Si substrate 1 reaches as high as 1200° C. to 1400° 0. The impurities, which are doped in the surface of the Si substrate 1 that is abnormally heated, diffuses and piles up at the interface of the gate insulation film 5 n. It is considered that the impurities, the concentration of which is further increased at the interface of the gate insulation film 5 n, permeates into the gate insulation film 5 n and a leakage path is formed.

Similarly, in the nMOSFET according to the comparative example 2-2, the impurity density in the surface of the Si substrate 1 becomes 1×10²¹ cm⁻³ or more. In addition, the overlap capacitance Cov between the end portion of the extension region 11 a, 11 b and the gate electrode 7 n further increases up to as high as 3×10⁻¹⁶ F/μm. However, since the conventional RTA is performed, abnormal heating at 1200° C. or more does not occur in the surface of the Si substrate 1. Thus, despite the high surface impurity density of the Si substrate and the high overlap capacitance Cov, the permeation of impurities into the gate insulation film 5 n is suppressed and the gate leakage current does not increase.

On the other hand, in the nMOSFET according to the second embodiment, the impurity density in the surface of the Si substrate 1 is suppressed to 3×10²⁰ cm⁻³ or less. Further, as shown in FIG. 36, the overlap capacitance Cov between the extension region 11 a, 11 b and the gate electrode 7 n is suppressed, and it was confirmed that the overlap capacitance Cov decreased to 1×10⁻¹⁶ F/μm.

It is thus considered that even if the instantaneous maximum temperature of the surface of the Si substrate 1 reached as high as 1200° C. to 1400° C. due to the very rapid annealing represented by flashtube annealing, the overlap capacitance Cov with the gate electrode 7 n was low and hence the amount of impurities permeating into the gate insulation film 5 n was suppressed and the gate leakage current did not increase.

FIG. 50 is a graph showing the relationship between the gate leakage current and the gate overlap capacitance Cov, with attention paid to the nMOSFET. The abscissa indicates the gate overlap capacitance, and the ordinate indicates the gate leakage current.

As shown in FIG. 50, it is understood that the gate leakage current decreases as the gate overlap capacitance Cov becomes smaller. However, in the case where the impurity density at the surface of the Si substrate 1 is 5×10¹⁹ cm⁻³ or less, the parasitic resistance increases and the current driving power becomes deficient. The same applies to the case where the end portion of the extension region 11 a, 11 b and the gate electrode 7 n are extremely spaced apart and, as a result, the gate overlap capacitance Cov decreases to 5×10⁻¹⁷ F/μm or less.

In the nMOSFETs according to the comparative example 2-1 and comparative example 2-2, high impurity density regions of the extension regions 11 a and 11 b are distributed in the vicinity of the channel region. Thus, the controllability of the gate electrode 7 n decreases, and the short-channel effect considerably increases. On the other hand, in the nMOSFET according to the second embodiment, the extension regions 11 a, 11 b are formed with an offset from the gate electrode 7 n by using the diffusion regions having a steep impurity density distribution. Hence, the offset gate structure with no bias offset can be realized, and the parasitic resistance in the region immediately under the sidewall spacer 21 n, 22 n can be decreased and a high current driving power can be obtained.

FIG. 51 is a graph showing a drain current versus a drain voltage, and FIG. 52 is a graph showing a drain current versus a gate voltage. FIGS. 51 and 52 show the cases in which the gate length of each of the nMOSFET according to the second embodiment and the nMOSFET according to the comparative example 2-1 is 30 nm.

As shown in FIGS. 51 and 52, in the second embodiment, no offset voltage occurs and a high drain current is obtained. In the second embodiment, even if the effective channel length is increased by the presence of the offset region, the channel mobility is high and thus the channel resistance is low. Hence, even in the case of the nMOSFET according to the comparative example 2-1, as compared with a MOSFET with a weaker short-channel effect and a greater channel length, it becomes possible to secure a high current driving power while reducing gate leakage current.

As has been described in connection with the semiconductor device fabrication method according to the second embodiment, when the very-rapid high-luminance optical heat treatment process is performed, the extension region 11 a, 11 b is offset from the gate electrode 7 n and the impurity density in the surface of the Si substrate 1 is decreased. Thereby, the permeation of impurities into the gate insulation film 5 n can be suppressed. Thus, without an increase in gate leakage current, an increase in resistance of the extension region 11 a, 11 b can be suppressed. As a result, the parasitic resistance can be reduced and kept at the reduced value, and the short-channel effect can be decreased. Hence, the controllability of the channel current by the gate electrode 7 n can be enhanced, and a high driving power can be obtained. In short, according to the second embodiment, the activation process for the extension region 11 a, 11 b with a wide process window relating to the heat treatment process can be realized, and a high-performance nMOSFET with a fine structure can easily be fabricated.

In the above description of the second embodiment, attention has been paid to the nMOSFET. Needless to say, the second embodiment is similarly applicable to the pMOSFET, and the same advantageous effect can be obtained.

(Modification of Second Embodiment)

In the above-described second embodiment, the annealing device was described as employing the xenon flashtube as the light source for light radiation. However, the second embodiment is not limited to this example, and the light source may be, for instance, any one of flashtubes using other rare gases, mercury and hydrogen, an arc discharge lamp, an excimer laser, an Ar laser, an N2 laser, a YAG laser, a titanium-sapphire laser, a CO laser, and a CO₂ laser.

In the above-described embodiment, the shallow-junction extension regions 11 a and 11 b are formed after the deep-junction source/drain regions 9 a and 9 b are formed. However, as shown in FIGS. 53 to 59, the shallow-junction extension regions 11 a and 11 b may first be formed, following which the deep-junction source/drain regions 9 a and 9 b may be formed. This fabrication method will now be described with reference to FIGS. 53 to 59. FIGS. 53 to 59 are cross-sectional views successively illustrating fabrication steps of a semiconductor device according to a modification of the second embodiment. FIGS. 53 to 59 correspond to FIGS. 26 to 33, with reference to which the first embodiment has been described.

To begin with, the above-described fabrication steps up to FIG. 37 are carried out, and the offset spacers 6 n, 6 p are formed of silicon oxide films.

Then, as shown in FIG. 53, using a photoresist 65 formed on the pMOSFET region, the gate electrode 7 n on the nMOSFET region and the offset spacers 6 n as a mask, atoms of Group V, e.g., arsenic (As) ions, which become n-type impurities, are implanted in the surface of the p-well region 2. The conditions for the ion implantation are, as in the second embodiment, an acceleration energy of 1.5 keV and a dosage of 1×10¹⁵ cm⁻².

Next, as shown in FIG. 54, using a photoresist 66 formed on the p-well region 2, the gate electrode 7 p and offset spacers 6 p as a mask, atoms of Group III, e.g., boron (B) ions, which become p-type impurities, are implanted in the surface of the n-well region 3. The conditions for the ion implantation are, as in the second embodiment, an acceleration energy of 0.3 keV and a dosage of 1×10¹⁵ cm⁻².

Subsequently, as shown in FIG. 55, a silicon oxide (SiO₂) film 15 is deposited by LPCVD at film formation temperatures of 600° C. or less. Further, a silicon nitride (Si₃N₄) film 16 is deposited on the silicon oxide (SiO₂) film 15 by LPCVD at film formation temperatures of 600° C. or less.

As shown in FIG. 56, using a flashtube as a heat source, an activation annealing process is performed. This step corresponds to the above-described step of FIG. 29. By this activation annealing process, shallow extension regions 11 a, 11 b, 12 a and 12 b are formed in regions in the Si substrate 1, which neighbor the gate electrodes 7 n and 7 p, offset spacers 6 n and 6 p and the device isolation regions 4.

In a subsequently step illustrated in FIG. 57, the silicon nitride film 16 and silicon oxide film 15 are completely removed by hot phosphoric acid and hydrofluoric acid. Then, a silicon nitride (Si₃N₄) film is deposited by LPCVD at film formation temperatures of 600° C. or less. The silicon nitride film is etched by a method of leaving sidewall parts thereof using RIE, and thus the silicon nitride film is selectively left on the side surfaces of the offset spacers 6 n, 6 p. Thereby, sidewall spacers 8 n, 8 p are formed of silicon nitride films. The offset spacers 6 n, 6 p may be formed of silicon nitride films, and the sidewall spacers 8 n, 8 p may be formed of silicon oxide films. Subsequently, a photoresist 67 is formed on the surface of the n-well region 3. Using the photoresist 67, gate electrode 7 n, offset spacers 6 n and sidewall spacers 8 n as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. By this ion implantation, the impurity ions of Group V atoms are also implanted in the gate electrode 7 n. The conditions for the ion implantation are, as in the second embodiment, an acceleration energy of 5 keV and a dosage of 3×10¹⁵ cm⁻². As Group V atoms to be implanted, arsenic (As) is also usable. However, in the case of using P, defects due to ion implantation can be remedied more easily by activation heat treatment, and a pn junction leakage current can be suppressed.

Subsequently, as shown in FIG. 58, using a photoresist 68 formed on the p-well region 2, gate electrode 7 p, offset spacers 6 p and sidewall spacers 8 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. By this ion implantation, the impurity ions of Group III atoms are also implanted in the gate electrode 7 p. The conditions for the ion implantation are, as in the second embodiment, an acceleration energy of 2 keV and a dosage of 3×10¹⁵ cm⁻². In the state immediately after the end of the ion implantation illustrated in FIGS. 57 and 58, inactive source/drain regions 109 a, 109 b, 110 a and 110 b are formed in regions in the Si substrate 1, which neighbor the offset spacers 6 n, 6 p and the device isolation regions 4.

Subsequently, as shown in FIG. 59, a silicon oxide (SiO₂) film 17 is deposited by LPCVD at film formation temperatures of 600° C. or less. Further, a silicon nitride (Si₃N₄) film 18 is deposited the silicon oxide (SiO₂) film 17 by LPCVD at film formation temperatures of 600° C. or less. Using a halogen lamp as a heat source, an activation annealing process for the inactive source/drain regions 109 a, 109 b, 110 a and 110 b is carried out. The condition for the activation annealing process is a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6 and, for example, RTA is conducted within 10 seconds at 1000° C. to 1050° C., or spike RTA is conducted with a peak temperature set at 1000° C. to 1050° C. By this activation annealing process, source/drain regions 9 a, 9 b, 10 a and 10 b, which are spaced apart from end portions of the gate electrodes 7 n, 7 p by a degree corresponding to the offset spacer 6 n, 6 p and sidewall spacer 8 n, 8 p and are in contact with the device isolation regions 4, are formed in the Si substrate 1. By this activation annealing process, the impurities, which are doped in the gate electrode 7 n, 7 p, can be diffused to the interface with the gate insulation film 5 n, 5 p, and crystal defects occurring in the Si substrate 1 due to ion implantation can be eliminated.

Thereafter, the sidewall spacers 23 n, 24 n, 23 p and 24 p are left so as to function to prevent a Ni silicide reaction in a later fabrication step. Thus, the basic structure of the semiconductor device according to the present modification is completed. The fabrication steps following the step of FIG. 59 are the same as those in the second embodiment, so a description thereof is omitted here. By the above-described fabrication method, too, the structure shown in FIG. 34 can be obtained.

(Third Embodiment)

Next, a semiconductor device and a method for fabricating the semiconductor device, according to a third embodiment of the invention, are described. FIG. 60 is a cross-sectional view of the semiconductor device according to the third embodiment.

As shown in FIG. 60, in the semiconductor device according to the third embodiment, the offset spacer 6 p of the pMOSFET is removed from the structure shown in FIG. 34, which has been described in connection with the second embodiment. Specifically, the third embodiment is configured such that the offset spacer 6 n, which has been described in connection with the second embodiment, is provided only in the nMOSFET in the structure shown in FIG. 1, which has been described in connection with the first embodiment.

As has been described in connection with the second embodiment, the presence of the offset spacer 6 n in the nMOSFET reduces the overlap capacitance Cov. By choosing the film thickness of the offset spacer 6 n in the range of about 1 to 10 nm, the gate overlap capacitance Cov per unit gate width can be set at about 1×10⁻¹⁵ F/μm to 1×10⁻¹⁶ F/μm. Representatively, the film thickness Δd of about 4 nm can be adopted. By contrast, no offset spacer is provided in the pMOSFET. Accordingly, the overlap capacitance Cov between the extension region 11 b and gate electrode 7 n is less than the overlap capacitance Cov between the extension region 12 a and the gate electrode 7 p for the pMOSFET. In the other structural aspects, the third embodiment is the same as the first or second embodiment.

FIG. 61 is a graph showing a cumulative probability of nMOSFETs versus a gate leakage current. In FIG. 61, respective curves are associated with wafers A to E each including a plurality of nMOSFETs. FIG. 61 shows a percentage (cumulative probability) of nMOSFETs, the gate leakage current of which is less than a certain value, in each wafer. FIG. 62 is a graph similar to the graph of FIG. 61, which relates to pMOSFETs. As is clear from the comparison between FIGS. 61 and 62, the nMOSFET has a higher gate leakage current than the pMOSFET, and the gate withstand voltage of the nMOSFET is worse.

FIGS. 63 and 64 are graphs (rolloff characteristics) showing gate threshold voltages Vth versus gate lengths L_(gate) of nMOSFETs and pMOSFETs, respectively. In the characteristics shown, the diffusion layer depth X_(j) of the extension region is set at X_(j)=15 n with respect to both the nMOSFET and pMOSFET. As is understood from FIGS. 63 and 64, the short-channel effect is worse in the nMOSFET than in the pMOSFET. In other words, in the case where the very rapid annealing is applied to the impurity activation step, the deterioration in characteristics becomes more conspicuous in the nMOSFET than in the pMOSFET, as the degree of microfabrication increases.

The reason why the gate withstand voltage of, the nMOSFET is worse than that of the pMOSFET is considered to be as follows. That is, in the nMOSFET, arsenic (As) or phosphorus (P), which has a great mass, is used as impurities for forming the diffusion layer. It is thus considered that in the nMOSFET, compared to the pMOSFET in which boron (B) is used, damage tends to easily occur due to impurity doping, and the light absorption ratio increases. As a result of the increase in light absorption ratio, it is considered that the annealing efficiency is enhanced, the impurities diffuse to the gate insulation film to form a leakage path, the gate withstand voltage deteriorates, and the impurities also diffuse in the lateral direction, leading to worsening in short-channel effect.

Next, a method for fabricating the semiconductor device according to the present embodiment is described with reference to FIGS. 65 to 81. FIGS. 65 to 81 are cross-sectional views successively illustrating fabrication steps of the semiconductor device according to this embodiment. The semiconductor device fabrication method to be described below is merely an example, and the semiconductor device of this embodiment may, needless to say, be fabricated by other various methods including modifications of the method described below. For example, in the description below, the gate electrodes 7 n, 7 p are formed of polycrystalline Si films according to the semiconductor device fabrication methods of the first and second embodiments. However, this is merely an example, and the gate electrodes 7 n, 7 p may be formed of polycrystalline SiGe (Ge concentration: 10 to 30 atomic %).

To start with, the fabrication steps of FIGS. 2 to 5, as described in connection with the first embodiment, are carried out. FIG. 65 is a cross-sectional view corresponding to the end of the fabrication step of FIG. 5. Subsequently, in this embodiment, offset spacers 6 n for the nMOSFET are formed. Specifically, as shown in FIG. 66, a silicon oxide (SiO₂) film 6 is formed on the gate electrodes 7 n, 7 p, Si substrate 1 and device isolation regions 4 by LPCVD at 600° C. or less within the range of film thickness of about 2 to 10 nm, for example, with a film thickness of 4 nm. In place of the silicon oxide film 6, a silicon nitride (Si₃N₄) film may be formed within the range of film thickness of about 2 to 10 nm, for example, with a film thickness of 4 nm.

In a subsequent step shown in FIG. 67, a photoresist film 45 is formed on the surface of the p-well region 2.

Then, as shown in FIG. 68, the silicon oxide film 6 on the pMOSFET region is etched away by diluted hydrofluoric acid. In the case where a silicon nitride film is used in place of the silicon oxide film 6, the silicon oxide film 6 on the pMOSFET region is etched away by hot phosphoric acid. Following this step, the photoresist 45 is removed, as shown in FIG. 69.

Next, as shown in FIG. 70, a photoresist film 46 is formed on the surface of the n-well region 3.

As shown in FIG. 71, the silicon oxide film 6 on the nMOSFET region is etched by RIE and selectively left on side surfaces of the gate electrode 7 n and gate insulation film 5 n. As a result, offset spacers 6 n, as shown in FIG. 71, are completed.

Following the above step, the photoresist film 46 is removed as shown in FIG. 72. As a result, a structure is realized wherein the offset spacers 6 n are formed on the side surfaces of the gate electrode 7 n and gate insulation film 5 n of the nMOSFET region, and no offset spacer is formed on side surfaces of the gate electrode 7 p and gate insulation film 5 p of the pMOSFET region.

Subsequently, the fabrication steps of FIGS. 7 to 18 which have been described in connection with the first embodiment (i.e., fabrication steps of FIGS. 38 to 47 described in connection with the second embodiment) are performed. Specifically, a silicon nitride (Si₃N₄) film is deposited by LPCVD at 600° C. or less. The silicon nitride film is etched by a method of leaving sidewall parts thereof using RIE. As a result, as shown in FIG. 73, sidewall spacers 8 n are formed on the side surfaces of the offset spacers 6 n in the nMOSFET region, and sidewall spacers 8 p are formed on the side surfaces of the gate electrode 7 p and gate insulation film 5 p in the pMOSFET region. Alternatively, the offset spacers 6 n may be formed of silicon nitride films, and the sidewall spacers 8 n, 8 p may be formed of silicon oxide films.

In the next fabrication step, as shown in FIG. 74, using a photoresist film 47 formed on the n-well region, the gate electrode 7 n, offset spacers 6 n and sidewall spacers 8 n as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. At this time, the ions of Group V atoms are also implanted in the gate electrode 7 n. The conditions for the ion implantation are an acceleration energy of 5 keV and a dosage of 3×10¹⁵ cm⁻². As Group V atoms to be implanted, arsenic (As) is also usable. However, in the case of using P, defects due to ion implantation can be remedied more easily by activation heat treatment, and a pn junction leakage current can be suppressed. The photoresist 47 is then removed.

Next, as shown in FIG. 75, using a photoresist film 48 formed on the p-well region 2, the gate electrode 7 p and sidewall spacers 8 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. At this time, the impurity ions of Group III atoms are also implanted in the gate electrode 7 p. The conditions for the ion implantation are an acceleration energy of 2 keV and a dosage of 3×10¹⁵ cm⁻².

By the ion implantation in FIGS. 74 and 75, inactive source/drain regions 109 a, 109 b, 110 a and 110 b are formed in the Si substrate 1. Then, an activation annealing process for the inactive source/drain regions 109 a, 109 b, 110 a and 110 b is performed by using a halogen lamp as a heat source. The condition for the activation annealing process is a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6 and, for example, RTA is conducted within 10 seconds at 1000° C. to 1050° C. or spike RTA is conducted with a peak temperature set at 1000° C. to 1050° C. By this activation annealing process, as shown in FIG. 76, a source/drain region 9 a, 9 b, which is spaced apart from an end portion of the gate electrode 7 n by a degree corresponding to the total thickness of the offset spacer 6 n and sidewall spacer 8 n and is in contact with the device isolation region 4, is formed in the p-well region 2. In addition, a source/drain region 10 a, 10 b, which is spaced apart from an end portion of the gate electrode 7 p by a degree corresponding to the thickness of the sidewall spacer 8 p and is in contact with the device isolation region 4, is formed in the Si substrate 1. By this activation annealing process, the impurities, which are doped in the gate electrode 7 n, 7 p, can be diffused to the interface with the gate insulation film 5 n, 5 p, and crystal defects occurring in the Si substrate 1 due to ion implantation can be eliminated. This fabrication step corresponds to the step of FIG. 10 which has been described in connection with the first embodiment.

Thereafter, as shown in FIG. 77, the sidewall spacers 8 n and 8 p, which are formed of silicon nitride, are removed by using hot phosphoric acid.

In the next step illustrated in FIG. 78, using a photoresist film 49 formed on the pMOSFET region, the gate electrode 7 n and offset spacers 6 n as a mask, atoms of Group V, e.g., arsenic (As), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. The conditions for the ion implantation are an acceleration energy of 5 keV and a dosage of 2×10¹⁴ cm⁻². The photoresist 49 is then removed.

As shown in FIG. 79, using a photoresist film 50 formed on the p-well region 2 and the gate electrode 7 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. The conditions for the ion implantation are an acceleration energy of 0.9 keV and a dosage of 2×10¹⁴ cm⁻². The fabrication steps of FIGS. 78 and 79 correspond to the fabrication steps of FIG. 12 and FIG. 13 in the first embodiment.

By the steps of FIGS. 78 and 79, inactive shallow extension regions 111 a, 111 b are formed in the p-well region 2. In addition, inactive shallow extension regions 112 a, 112 b are formed in the n-well region 3.

Subsequently, as shown in FIG. 80, a silicon oxide (SiO₂) film 13 and a silicon nitride (Si₃N₄) film 14 are successively deposited by LPCVD at 600° C. or less. Using a flashtube as a heat source, an activation annealing process is performed. As the condition for the activation annealing process, the relationship between the heat treatment temperature and heat treatment time, which is indicated in the hatched region in the double-logarithmic graph of FIG. 6, is preferable. In particular, the condition of the temperature range of 1100° C. or above is preferable. In this case, the Si substrate 1 is placed on a hot plate. In the state in which the Si substrate 1 is heated (auxiliary heating) from the back side, the upper surface of the Si substrate 1 should preferably be heated by heat emitted from the flashtube light source. This annealing process step is the same as the step of FIG. 17 which has been described in connection with the first embodiment. By the annealing process, shallow extension regions 11 a and 11 b are formed in the Si substrate 1 with an offset of a distance from an end portion of the gate electrode 7 n, which corresponds to the thickness of the offset spacer 6 n. In addition, shallow extension regions 12 a and 12 b are formed in the n-well region 3 with no intended offset from an end portion of the gate electrode 7 p.

In a subsequently step illustrated in FIG. 81, the silicon nitride film 14 and silicon oxide film 13 are etched by RIE. Thereby, in the nMOSFET region, the silicon nitride film 14 and silicon oxide film 13 are selectively left on the side surfaces of the offset spacers 6 n. In addition, in the pMOSFET region, the silicon nitride film 14 and silicon oxide film 13 are selectively left on the side surfaces of the gate electrode 7 p and gate insulation film 5 p. Alternatively, after the silicon nitride film 14 and silicon oxide film 13 are completely removed by hot phosphoric acid and hydrofluoric acid or after the uppermost-layer silicon nitride film 14 is removed by hot phosphoric acid, a silicon nitride film and a silicon oxide film, for instance, may newly be formed. In this case, the silicon nitride film and silicon oxide film are etched by RIE and selectively left on the side surfaces of the offset spacer 6 n in the nMOSFET region, and selectively left on the side surfaces of the side surfaces of the gate electrode 7 p and gate insulation film 5 p in the pMOSFET region. Thereby, sidewall spacers 21 n, 21 p, 22 n and 22 p are completed. This fabrication step corresponds to the step of FIG. 18 which has been described in connection with the first embodiment.

The subsequent fabrication steps are the same as those of the semiconductor device fabrication methods according to the first and second embodiments, and a description thereof is omitted here. By the above-described process, the semiconductor device with the CMOS structure, as shown in the cross section of FIG. 60, which includes the extension regions 11 a, 11 b, 12 a, 12 b each having a junction depth of 20 nm or less, is completed.

According to the semiconductor device fabrication method of the third embodiment of the invention, the gate overlap capacitance Cov can preferentially be reduced in the nMOSFET having a low gate withstand voltage and poor rolloff characteristics. Therefore, the characteristics of the nMOSFET can independently be enhanced without degrading the current driving power of the pMOSFET.

(Fourth Embodiment)

Next, a semiconductor device and a method for fabricating the semiconductor device, according to a fourth embodiment of the invention, are described. FIG. 82 is a cross-sectional view of the semiconductor device according to the fourth embodiment.

As shown in FIG. 82, in the semiconductor device according to the fourth embodiment, the thickness of the offset spacer 6 p of the pMOSFET is made less than the thickness of the offset spacer 6 n of the nMOSFET in the structure shown in FIG. 34, which has been described in connection with the second embodiment. In the description below, the offset spacers of the nMOSFET according to the present embodiment are referred to as “offset spacers 6 na”, and the offset spacers of the pMOSFET are referred to as “offset spacers 6 pa”.

The present embodiment is based on the following concept. As has been described in connection with the third embodiment, the gate withstand voltage of the nMOSFET is lower than that of the pMOSFET (see FIGS. 61 and 62) and the short-channel effect of the nMOSFET is worse than that of the pMOSFET (see FIGS. 63 and 64). In other words, in the case where the very rapid annealing technique is applied to the impurity activation step, the deterioration in characteristics becomes more conspicuous in the nMOSFET than in the pMOSFET, as the degree of microfabrication becomes higher. As a measure to cope with this problem, in the third embodiment, the offset spacers 6 n are provided only in the nMOSFET. On the other hand, in the present fourth embodiment, the thickness of the offset spacer is made different between the nMOSFET and pMOSFET, and the thickness of the offset spacer 6 na is made greater than that of the offset spacer 6 pa.

Next, a method for fabricating the semiconductor device shown in FIG. 82 is described with reference to FIGS. 83 to 97. FIGS. 83 to 97 are cross-sectional views successively illustrating fabrication steps of the semiconductor device shown in FIG. 82. The semiconductor device fabrication method to be described below is merely an example, and the semiconductor device of this embodiment may be fabricated by other various methods. For example, in the description below, the gate electrodes 7 n, 7 p are formed of polycrystalline Si films according to the semiconductor device fabrication methods of the first and second embodiments. However, the gate electrodes 7 n, 7 p may be formed of polycrystalline SiGe (Ge concentration: 10 to 30 atomic %).

To start with, the fabrication steps up to the step of FIG. 69, as described in connection with the third embodiment, are carried out, and a silicon oxide film 6 is formed on the p-well region 2. Subsequently, as shown in FIG. 83, a silicon oxide (SiO₂) film 6 v with a thickness of about 1 to 5 nm is formed on the silicon oxide film 6 of the nMOSFET region and on the gate electrode 7 n, Si substrate 1 and device isolation regions 4 in the pMOSFET region by LPCVD at 600° C. or less. In place of the silicon oxide film 6 v, a silicon nitride (Si₃N₄) film may be deposited.

Assume now that the thickness of the silicon oxide film 6 that is deposited in the step of FIG. 66 is set at about 4 nm, and the thickness of the silicon oxide film 6 v that is deposited in the step of FIG. 83 is set at 2 nm. In this case, in the nMOSFET region, the silicon oxide film with a thickness of 6 nm, which is the total thickness of the silicon oxide film 6 and silicon oxide film 6 v, is formed. In the pMOSFET region, the silicon oxide film with a thickness of 2 nm, which is the thickness of only the silicon oxide film 6 v, is formed. For the purpose of convenience, FIG. 83 depicts the composite film of the silicon oxide film 6 and silicon oxide film 6 v in the nMOSFET region as if the silicon oxide film 6 v was formed. Actually, however, the silicon oxide film 6 v that is shown is a double-layer stacked film of the silicon oxide layers 6 and 6 v. In the meantime, films with different dielectric constants may be deposited. For example, a silicon oxide film 6 may be deposited in the step of FIG. 66, and a silicon nitride film 6 v may be deposited in the step of FIG. 83.

In a subsequent step shown in FIG. 84, a photoresist film 69 is formed on the surface of the p-well region 2.

Then, as shown in FIG. 85, the silicon oxide film 6 v on the pMOSFET region is etched by a method of leaving sidewall parts thereof using RIE, and thus the thin silicon oxide film 6 v is subjected to directive etching. As a result, the thin silicon oxide film 6 v is selectively left on the side surfaces of the gate electrode 7 p and gate insulation film 5 p, and offset spacers 6 pa are completed. Then, the photoresist 69 is removed.

Next, as shown in FIG. 86, a photoresist film 70 is formed on the n-well region 3.

As shown in FIG. 87, the silicon oxide film 6 v on the nMOSFET region is etched by a method of leaving sidewall parts thereof using RIE, and thus the thick silicon oxide film 6 v is subjected to directive etching. As a result, the thick silicon oxide film 6 v is selectively left on the side surfaces of the gate electrode 7 n and gate insulation film 5 n, and offset spacers 6 na are completed. Then, the photoresist 70 is removed. As a result, the offset spacers 6 na with a thickness of 6 nm are formed in the nMOSFET region, and the offset spacers 6 pa with a thickness of 2 mm are formed in the pMOSFET region.

Subsequently, the fabrication steps of FIGS. 7 to 18 which have been described in connection with the first embodiment (i.e., fabrication steps of FIGS. 38 to 47 described in connection with the second embodiment; or fabrication steps of FIGS. 73 to 81 described in connection with the third embodiment) are performed. Specifically, a silicon nitride (Si₃N₄) film is deposited by LPCVD at 600° C. or less. The silicon nitride film is etched by a method of leaving sidewall parts thereof using RIE, and is selectively left on side surfaces of the offset spacers 6 na, 6 pa. As a result, as shown in FIG. 88, sidewall spacers 8 n, 8 p are formed on the side surfaces of the offset spacers 6 na, 6 pa. Alternatively, the offset spacers 6 na, 6 pa may be formed of silicon nitride films, and the sidewall spacers 8 n, 8 p may be formed of silicon oxide film.

In the next fabrication step, as shown in FIG. 89, using a photoresist film 61 formed on the n-well region 3, the gate electrode 7 n, offset spacers 6 na and sidewall spacers 8 n as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. At this time, the ions of Group V atoms are also implanted in the gate electrode 7 n. The conditions for the ion implantation are the same as has been described with reference to FIG. 8 in connection with the first embodiment. The photoresist 61 is then removed.

Next, as shown in FIG. 90, using a photoresist film 62 formed on the p-well region 2, the gate electrode 7 p, offset spacers 6 pa and sidewall spacers 8 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. This fabrication step is the same as has been described with reference to FIG. 9 in connection with the first embodiment.

By the ion implantation in FIGS. 89 and 90, inactive source/drain regions 109 a and 109 b are formed in those portions of the p-well region 2, which neighbor the offset spacers 6 na and device isolation regions 4. In addition, inactive source/drain regions 110 a and 110 b are formed in those portions of the n-well region 3, which neighbor the offset spacers 6 pa and device isolation regions 4. Then, an activation annealing process for the inactive source/drain regions 109 a, 109 b, 110 a and 110 b is performed by using a halogen lamp as a heat source. The condition for the activation annealing process is a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6 and, for example, RTA is conducted within 10 seconds at 1000° C. to 1050° C. or spike RTA is conducted with a peak temperature set at 1000° C. to 1050° C. This annealing process is the same as has been described with reference to FIG. 10 in connection with the first embodiment. By this annealing process, as shown in FIG. 91, source/drain regions 9 a, 9 b, 10 a, and 10 b, which are spaced apart from end portions of the gate electrodes 7 n, 7 p and are in contact with the device isolation region 4, are formed in the Si substrate 1.

Thereafter, as shown in FIG. 92, the sidewall spacers 8 n and 8 p, which are formed of silicon nitride, are removed by using hot phosphoric acid.

In the next step illustrated in FIG. 93, using a photoresist film 63 formed on the n-well region 3, the gate electrode 7 n and offset spacers 6 na as a mask, atoms of Group V, e.g., arsenic (As), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. The conditions for the ion implantation are an acceleration energy of 5 keV and a dosage of 2×10¹⁴ cm⁻². This fabrication step corresponds to the step of FIG. 12 in the first embodiment. The photoresist 63 is then removed.

As shown in FIG. 94, using a photoresist film 64 formed on the p-well region 2, the gate electrode 7 p and offset spacers 6 pa as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. The conditions for the ion implantation are an acceleration energy of 0.9 keV and a dosage of 2×10¹⁴ cm⁻².

By the steps of FIGS. 93 and 94, inactive shallow extension regions 111 a, 111 b, 112 a and 112 b are formed in those portions of the p-well region 2 and n-well region 3, which neighbor the gate electrodes 7 n, 7 p and device isolation regions 4.

Subsequently, as shown in FIG. 95, a silicon oxide (SiO₂) film 13 and a silicon nitride (Si₃N₄) film 14 are successively deposited by LPCVD at film formation temperatures of 600° C. or less.

As shown in FIG. 96, using a flashtube as a heat source, an activation annealing process is performed. As the condition for the activation annealing process, the relationship between the heat treatment temperature and heat treatment time, which is indicated in the hatched region in the double-logarithmic graph of FIG. 6, is preferable. In particular, the condition of the temperature range of 1100° C. or more is preferable. This fabrication step is the same as the step of FIG. 17 which has been described in connection with the first embodiment. By this activation annealing process, shallow extension regions 11 a and 11 b, which neighbor the offset spacers 6 na, and shallow extension regions 12 a and 12 b, which neighbor the offset spacers 6 pa, are formed.

In a subsequently step illustrated in FIG. 97, the silicon nitride film 14 and silicon oxide film 13 are etched by RIE, and are selectively left on the side surfaces of the offset spacers 6 na, 6 pa. Alternatively, after the silicon nitride film 14 and silicon oxide film 13 are completely removed by hot phosphoric acid and hydrofluoric acid or after the uppermost-layer silicon nitride film 14 is removed by hot phosphoric acid, a silicon nitride film and a silicon oxide film, for instance, may newly be formed and selectively left by RIE on the side surfaces of the offset spacers 6 na, 6 pa. Thereby, as shown in FIG. 97, sidewall spacers having the stacked structure comprising the silicon oxide film 21 n, 21 p and silicon nitride film 22 n, 22 p or sidewall spacers having the single-layer structure comprising the silicon oxide film or silicon nitride film are formed. The thickness of the insulation film excluding the offset spacer 6 na, 6 pa, which finally becomes the sidewall spacer, is set at 20 to 40 nm as the thickness of the silicon oxide film 21 n, 21 p and silicon nitride film 22 n, 22 p combined.

The subsequent fabrication steps are the same as those in the first to third embodiments, and a description thereof is omitted here. By the above-described process, the semiconductor device with the CMOS structure, as shown in FIG. 82, which includes the extension regions 11 a, 11 b, 12 a, 12 b each having a junction depth of 20 nm or less, is completed.

According to the fourth embodiment, the gate overlap capacitance Cov can preferentially be reduced in the nMOSFET having a low gate withstand voltage and poor rolloff characteristics. Therefore, the characteristics of the nMOSFET can independently be enhanced without degrading the current driving power of the pMOSFET.

(Fifth Embodiment)

Next, a semiconductor device and a method for fabricating the semiconductor device, according to a fifth embodiment of the invention, are described. As in the first to fourth embodiments, the first conductivity type and second conductivity type in the description below are mutually opposite conductivity types. In the description below, it is assumed that the first conductivity type is p-type and the second conductivity type is n-type. Alternatively, the first conductivity type may be n-type and the second conductivity type may be p-type. FIG. 98 is a cross-sectional view of a semiconductor device according to the fifth embodiment of the invention.

As shown in FIG. 98, in the semiconductor device according to the fifth embodiment, the gate insulation films 5 p, 5 n in the structure shown in FIG. 1, which has been described in connection with the first embodiment, are replaced with stacked structures comprising first gate insulation films 71 n, 71 p and second gate insulation films 72 n, 72 p. The first gate insulation films 71 n, 71 p are formed of SiO₂ films or silicon oxynitride films (SiON films). The second gate insulation films 72 n, 72 p are formed of SiN films, Si₃N₄ films or SiON films. The nitrogen concentration in the first gate insulation film 71 n, 71 p is lower than that in the second gate insulation film 72 n, 72 p. In the case where the first gate insulation film 71 n, 71 p is formed of an SiON film, it is preferable that the nitrogen concentration in the surface portion of the first gate insulation film 71 n, 71 p be set at 15 atomic % or less.

A gate electrode 77 n of an n-channel insulated-gate transistor, which is 50 to 150 nm thick, is of the second conductivity type (n-type) and is formed of polycrystalline Si or polycrystalline SiGe (Ge concentration: 10 to 30 atomic %), is provided on the second gate insulation film 72 n. Sidewall spacers 21 n are formed on side walls of the gate electrode 77 n, first gate insulation film 71 n and second gate insulation film 72 n.

A gate electrode 77 p of a p-channel insulated-gate transistor, which is 50 to 150 nm thick, is of the first conductivity type (p-type) and is formed of polycrystalline Si or polycrystalline SiGe (Ge concentration: 10 to 30 atomic %), is provided on the second gate insulation film 72 p. Sidewall spacers 21 p are formed on side walls of the gate electrode 77 p, first gate insulation film 71 p and second gate insulation film 72 p.

In the other structural aspects, the fifth embodiment is the same as the first embodiment, so a description of common parts is omitted here.

FIG. 99 is a graph in which the abscissa indicates positions and the ordinate plots the nitrogen concentration in the second gate insulation film 72 n. As shown in FIG. 99, the nitrogen concentration in the second gate insulation film 72 n is 57 atomic % at maximum, and the nitrogen concentration in the second gate insulation film 72 n is higher than that in the first gate insulation film 71 n. The maximum nitrogen concentration of 57 atomic % corresponds to the nitrogen concentration of 4/(3+4)=57 of the Si₃N₄ film with a stoichiometric composition. The nitrogen concentration in the first gate insulation film 71 n is 15 atomic % at maximum, and the nitrogen concentration in the second gate insulation film 72 n may take a value within a range of 20 to 57 atomic %.

If the nitrogen concentration in the second gate insulation film 72 n decreases below 20 atomic %, the gate leakage current increases disadvantageously. If the nitrogen concentration in the second gate insulation film 72 n is increased to 30 atomic % or more, the gate leakage current is advantageously further reduced. However, if the nitrogen concentration in the second gate insulation film 72 n exceeds 57 atomic %, the mobility deteriorates. As a result, the mutual conductance gm of the n-channel insulated-gate transistor disadvantageously decreases.

Next, a semiconductor device fabrication method according to the fifth embodiment is described. The fabrication method according to the fifth embodiment is substantially the same as the method illustrated in FIGS. 2 to 18 in connection with the first embodiment.

As shown in FIG. 2, after device isolation regions 4 are formed, desired impurities are ion-implanted in regions corresponding to channel portions, and these regions are electrically activated and a p-well region 2 and an n-well region 3 are formed.

Next, SiO₂ is formed by thermal oxidation on the surfaces of the p-well region 2 and n-well region 3, and thus first gate insulation films 71 n, 71 p are formed. Alternatively, SiON(N concentration in surface layer <15 atomic %) is formed by LPCVD on the surfaces of the p-well region 2 and n-well region 3, and thus first gate insulation films 71 n, 71 p are formed.

Subsequently, one to three atomic layers of SiN films or Si₃N₄ films, the nitrogen concentration of which is higher than that of the first gate insulation films 71 n, 71 p (>20 atomic %), are deposited on the first gate insulation films 71 n, 71 p by atomic layer deposition (ALD) using alternate introduction of dichlorosilane (SiH₂Cl₂) gas and ammonia (NH₃) gas. The deposited SiN films or Si₃N₄ films are formed as second gate insulation films 72 n, 72 p. In another method, oxygen (O₂) is further added to SiH₂Cl₂ gas and NH₃ gas, and one to three atomic layers of SiON(N concentration: 20 atomic % or more) are deposited and formed as second gate insulation films 72 n, 72 p.

In a subsequent fabrication step similar to the step of FIG. 3, a gate electrode film 77 with a thickness of 50 to 150 nm is formed on the second gate insulation film 72 n, 72 p by LPCVD using, e.g., polycrystalline Si film or polycrystalline SiGe (Ge concentration: 10 to 30 atomic %) as a material. The gate insulation film 5 in FIG. 3 corresponds to the stacked film of the first gate insulation film 71 n and second gate insulation film 72 n and the stacked film of the first gate insulation film 71 p and second gate insulation film 72 p in the present embodiment. The polycrystalline Si film 7 in FIG. 3 corresponds to the gate electrode film 77 in the present embodiment.

Further, in a subsequent fabrication step similar to the step of FIG. 3, using a photoresist film 51 as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the n-channel insulated-gate transistor with a dosage of 4×10¹⁵ to 8×10¹⁵ cm⁻².

Then, as in the step of FIG. 4, using a photoresist film 52 as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the p-channel insulated-gate transistor with a dosage of 4×10¹⁵ to 8×10¹⁵ cm⁻².

Subsequently, as in the step of FIG. 5, the gate electrode film 77, the second gate insulation film 72 n, 72 p and the first gate insulation film 71 n, 71 p are selectively processed (patterned) by successive reactive ion etching (RIE). Further, an annealing process is performed under a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6. In particular, the condition of the temperature range of 1100° C. or less is preferable. For example, RTA is conducted within a retention time of 10 seconds at 1000° C. to 1050° C. or spike RTA is conducted with a peak temperature set at 1000° C. to 1050° C. Thereby, the impurities, which are ion-implanted in the steps of FIGS. 3 and 4, are diffused uniformly in the entire gate electrode layer, of which the gate electrode 77 n for the nMOSFET and the gate electrode 77 p for the pMOSFET are formed, so that the diffusion may reach the interface with the second gate insulation films 72 n, 72 p.

Subsequently, as in the step of FIG. 7, a silicon nitride film is used as a material, and sidewall spacers 8 n, 8 p are formed on side walls of the gate electrode 77 n, 77 p, first gate insulation film 71 n, 71 p and second gate insulation film 72 n, 72 p.

In the next fabrication step, as in the step of FIG. 8, using a photoresist film 53 on the n-well region 3, gate electrode 77 n and sidewall spacers 8 n as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. By this ion implantation, the impurity ions of Group V atoms are also implanted in the gate electrode 77 n. The conditions for the ion implantation are an acceleration energy of 5 keV and a dosage of 3×10¹⁵ cm⁻². The photoresist film 53 is then removed.

Next, as in the step of FIG. 9, using a photoresist 54 formed on the p-well region 2, gate electrode 77 p and sidewall spacers 8 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. By this ion implantation, the impurity ions of Group III atoms are also implanted in the gate electrode 77 p. The conditions for the ion implantation are an acceleration energy of 2 keV and a dosage of 3×10¹⁵ cm⁻².

Next, the inactive source/drain regions formed in the steps of FIGS. 8 and 9 are activated. Specifically, using a halogen lamp as a heat source, an activation annealing process for the inactive source/drain regions is performed. The condition for the activation annealing process is a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6 and, for example, the annealing is conducted within 10 seconds at 1000° C. By this activation annealing process, as in the step of FIG. 10, source/drain regions 9 a, 9 b, 10 a and 10 b are formed. By this activation annealing process, the impurities, which are doped in the gate electrode 77 n, 77 p, can be diffused to the interface with the gate insulation film 72 n, 72 p, and crystal defects occurring in the Si substrate 1 due to ion implantation can be eliminated.

Thereafter, in the same step as shown in FIG. 11, the sidewall spacers 8 n and 8 p are removed by using hot phosphoric acid.

In the next step similar to the step of FIG. 12, using a photoresist film 55 formed on the n-well region 3 and the gate electrode 77 n as a mask, atoms of Group V, e.g., arsenic (As), which become n-type impurities, are ion-implanted in the surface of the p-well region 2 on the surface of the Si substrate 1. The conditions for the ion implantation are an acceleration energy of 1.5 keV and a dosage of 1×10¹⁵ cm⁻². The photoresist film 55 is then removed.

In the next step similar to the step of FIG. 13, using a photoresist film 56 formed on the p-well region 2 and the gate electrode 77 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. The conditions for the ion implantation are an acceleration energy of 0.3 keV and a dosage of 1×10¹⁵ cm⁻².

FIG. 14 shows the state immediately after the ion implantation in FIG. 12 and FIG. 13. In this state, inactive shallow extension regions 111 a, 111 b, 112 a and 112 b are formed in regions in the Si substrate 1, which neighbor the gate electrodes 77 n and 77 p and the device isolation regions 4.

Subsequently, as in the steps of FIGS. 15 and 16, a silicon oxide film 13 and a silicon nitride film 14 are successively formed.

Thereafter, as in the step of FIG. 17, using a flashtube as a heat source, an activation annealing process is performed. For the activation annealing process, the relationship between the heat treatment temperature and heat treatment time, which is indicated in the hatched region in the double-logarithmic graph of FIG. 6, is preferable. By the activation annealing process, shallow-junction extension regions 11 a and 12 b and shallow-junction extension regions 11 b and 12 a are formed in the Si substrate 1.

In a subsequent step similar to the step of FIG. 18, the silicon nitride film 14 and silicon oxide film 13 are etched by RIE, and sidewall spacers 21 n, 22 n are formed on the side walls of the gate electrode 77 n, and sidewall spacers 21 p, 22 p are formed on the side walls of the gate electrode 77 p. The subsequent fabrication steps are the same as described in connection with the first embodiment. The description of the subsequent steps of the first embodiment is applicable to the present embodiment if the term “gate electrode 7 n, 7 p” is changed to “gate electrode 77 n, 77 p” and the term “gate insulation film 5 n, 5 p” is changed to “gate insulation film 71 n, 72 n, 71 p, 72 p”.

By the above-described process, the semiconductor device with the CMOS structure, as shown in FIG. 98, which includes the extension regions 11 a, 11 b, 12 a, 12 b each having a junction depth of 20 nm or less, is completed. In the RTA in the semiconductor device fabrication method according to the fifth embodiment, the xenon flashtube is used as the light source for light radiation. Alternatively, it is possible to use, as the light source, for instance, any one of flashtubes using other rare gases, mercury and hydrogen, an arc discharge lamp, an excimer laser, an Ar laser, an N2 laser, a YAG laser, a titanium-sapphire laser, a CO laser, and a CO₂ laser.

FIG. 100 is a graph showing the relationship between gate leakage current and gate depletion ratio in the n-channel insulated-gate transistor according to the fifth embodiment of the invention and a conventional n-channel insulated-gate transistor. The term “gate depletion ratio” is defined by a ratio between the gate capacitance in the case where an inversion layer is formed in the channel and the gate capacitance in the case where an accumulation layer (in which majority carriers are accumulated) is formed in the channel. In FIG. 100, black solid circle marks indicate the present embodiment, and white circle marks indicate the prior art.

As shown in FIG. 100, in the case of the prior art, if the gate leakage current is reduced to 1×10⁻⁵ A or less, which is a level of no problem, the gate depletion ratio rises to 5% or more. As a result, a decrease in current driving power occurs due to non-uniformity in transistor characteristics of n-channel insulated-gate transistors and an increase in effective film thickness of gate insulation films.

By contrast, in the present embodiment, in the n-channel insulated-gate transistor, deterioration of the second gate insulation film 72 n and first gate insulation film 71 n due to phosphorus (P) can be suppressed. Therefore, as shown in FIG. 100, even if the dosage of P is high, the gate leakage current is low and good characteristics with a gate leakage current of 1×10⁻⁵ A or less and a gate depletion ratio of 1% or less can be obtained.

In the above descriptions of the semiconductor device and the fabrication method according to the fifth embodiment, the examples and effects have been described with attention paid to the n-channel insulated-gate transistor. Needless to say, the same advantageous effects can be obtained by applying the same techniques to the p-channel insulated-gate transistor.

(Sixth Embodiment)

Next, a semiconductor device and a method for fabricating the semiconductor device, according to a sixth embodiment of the invention, are described. As in the first to fifth embodiments, the first conductivity type and second conductivity type in the description below are mutually opposite conductivity types. In the description of the sixth embodiment, it is assumed that the first conductivity type is p-type and the second conductivity type is n-type. Alternatively, the first conductivity type may be n-type and the second conductivity type may be p-type. FIG. 101 is a cross-sectional view of a semiconductor device according to the sixth embodiment of the invention.

As shown in FIG. 101, in the semiconductor device according to the sixth embodiment, the gate electrodes 7 n, 7 p in the structure shown in FIG. 1, which has been described in connection with the first embodiment, are replaced with gate electrodes 78 n, 78 p, and also the gate insulation films 5 n, 5 p are replaced with gate insulation films 73 n, 73 p.

The gate insulation film 73 n functions as a gate insulation film of the nMOSFET, and is formed of an SiO₂ film or an SiON film, the nitrogen concentration of a surface layer of which is lower than 15 atomic %. The “surface layer” of the gate insulation film, in this context, refers to a surface region which is located not on the semiconductor substrate side but on the gate electrode side and is in contact with the gate electrode.

The gate electrodes 78 n, 78 p are formed on the gate insulation films 73 n, 73 p, respectively, using polycrystalline silicon including nitrogen atoms or polycrystalline SiGe (Ge concentration: 10 to 30 atomic %) including nitrogen atoms. The thickness of the gate electrode 78 n, 78 p is about 50 to 150 nm. The polycrystalline Si or polycrystalline SiGe includes atomic nitrogen in an amount of about 1×10¹⁸ cm⁻³ to 1×10²⁰ cm⁻³. The term “atomic nitrogen” refers to nitrogen in a state in which nitrogen does not form a compound crystal with silicon or germanium and is included in an Si crystal or SiGe crystal as impurities or the like. In the case where the concentration of atomic nitrogen is less than 1×10¹⁸ cm⁻³, the gate leakage current disadvantageously increases. In the case where the concentration of atomic nitrogen is higher than 1×10²⁰ cm⁻³, the gate depletion ratio increases and, as a result, the current driving power disadvantageously decreases due to non-uniformity in transistor characteristics and an increase in effective film thickness of gate insulation films. The range of atomic nitrogen between about 5×10¹⁸ cm⁻³ to 8×10¹⁹ cm⁻³ is more preferable since the suppression of gate leakage current becomes more conspicuous and the gate depletion ratio decreases.

Sidewall spacers 21 n are formed of silicon oxide films on both side surfaces of the gate electrode 78 n and gate insulation film 73 n, and further sidewall spacers 22 n are formed of silicon nitride films. In addition, sidewall spacers 21 p are formed of silicon oxide films on both side surfaces of the gate electrode 78 p and gate insulation film 73 p, and further sidewall spacers 22 p are formed of silicon nitride films.

In the other structural aspects, the sixth embodiment is the same as the first embodiment.

Next, a semiconductor device fabrication method according to the sixth embodiment is described. The fabrication method according to the sixth embodiment is substantially the same as the semiconductor device fabrication method according to the first embodiment, except for the formation of the gate insulation films 73 n, 73 p and gate electrodes 78 n, 78 p.

As shown in FIG. 2, after device isolation regions 4 are formed, desired impurities are ion-implanted in regions corresponding to channel portions, and these regions are electrically activated and a p-well region 2 and an n-well region 3 are formed.

Next, SiO₂ is formed by thermal oxidation, or SiON (N concentration in surface layer <15%) is formed by CVD, on the surfaces of the p-well region 2 and n-well region 3, and thus gate insulation films 73 n, 73 p are formed.

In a subsequent fabrication step similar to the step of FIG. 3, a gate electrode film 78 with a thickness of 50 to 150 nm, such as a polycrystalline Si film or polycrystalline SiGe (Ge concentration: 10 to 30 atomic %), is formed on the gate insulation film 73 n, 73 p by LPCVD. Specifically, the gate insulation film 5 in FIG. 3 corresponds to the gate insulation film 73 n, 73 p in the present embodiment, and the polycrystalline Si film 7 in FIG. 3 corresponds to the gate electrode film 78 in the present embodiment.

Thereafter, nitrogen ions are implanted in the gate electrode film 78 with an acceleration energy of 1 to 5 keV and a dosage of about 5×10¹³ cm⁻² to 5×10¹⁴ cm⁻², preferably 8×10¹³ cm⁻² to 3×10¹⁴ cm⁻². Then, the resultant structure is heated at about 500° C. to 1000° C., and the nitrogen is diffused to the bottom portion of the gate electrode film 78 of polycrystalline Si or polycrystalline SiGe.

Further, in a subsequent fabrication step similar to the step of FIG. 3, using a photoresist film 51 as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the n-channel insulated-gate transistor with a dosage of, e.g., 4×10¹⁵ to 8×10¹⁵ cm⁻².

Then, as in the step of FIG. 4, using a photoresist film 52 as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the p-channel insulated-gate transistor with a dosage of, e.g., 4×10¹⁵ to 8×10¹⁵ cm⁻².

Subsequently, the steps of FIGS. 5 to 18, which have been described in connection with the first embodiment, are performed. Needless to say, the description of the subsequent steps of the first embodiment is applicable to the present embodiment if the term “gate insulation film 5 n, 5 p” is changed to “gate insulation film 73 n, 73 p”, and the term “gate electrode 7 n, 7 p” is changed to “gate electrode 78 n, 78 p”. By the above-described process, the semiconductor device with the CMOS structure, as shown in FIG. 101, which includes the extension regions 11 a, 11 b, 12 a, 12 b each having a junction depth of 20 nm or less, is completed.

In the RTA in the semiconductor device fabrication method according to the sixth embodiment, the xenon flashtube is used as the light source for light radiation. Alternatively, it is possible to use, as the light source, for instance, any one of flashtubes using other rare gases, mercury and hydrogen, an arc discharge lamp, an excimer laser, an Ar laser, an N2 laser, a YAG laser, a titanium-sapphire laser, a CO laser, and a CO₂ laser.

FIG. 102 is a graph showing the relationship between gate leakage current and gate depletion ratio with respect to the n-channel insulated-gate transistor according to the sixth embodiment of the invention and a conventional n-channel insulated-gate transistor. In FIG. 102, black solid circle marks indicate the present embodiment, and white circle marks indicate the prior art.

As shown in FIG. 102, in the case of the prior art, if the gate leakage current is reduced to 1×10⁻⁵ A or less, which is a level of no problem, the gate depletion ratio rises to 5% or more. As a result, a decrease in current driving power occurs due to non-uniformity in transistor characteristics and an increase in effective film thickness of gate insulation films.

By contrast, in the present embodiment, deterioration of the gate insulation film 73 n due to phosphorus (P) can be suppressed. Therefore, even if the dosage of P is high, the gate leakage current is low. As a result, good characteristics with a gate leakage current of 1×10⁻⁵ A or less and a gate depletion ratio of 2% or less can be obtained.

In the above description, the nitrogen concentration in the surface portion of the gate insulation film 73 n, 73 p is less than 15 atomic %. However, the nitrogen concentration may be 15 atomic % or more. In this case, the effect of reduction in gate leakage current becomes conspicuous. Specifically, a remarkable improvement was found at a nitrogen concentration of 20 atomic % or more. Preferably, when the nitrogen concentration was set at 30 atomic % or more, the MOS characteristics were stabilized and the non-uniformity in transistor characteristics was decreased. The reason for this is that with an increase in nitrogen concentration, even if P and As come in contact at high concentration, it becomes possible to advantageously prevent fluidization of the gate insulation film 73 n, local reduction in film thickness or formation of pinholes. Thus, by raising the substrate auxiliary heating temperature without varying the impurity density of P in polycrystalline Si for forming the gate electrode 78 n, the sheet resistance of the extension region 11 a, 11 b can be reduced. As a result, the process window relating to the heat treatment step can be increased.

According to the semiconductor device fabrication method of the sixth embodiment of the invention, the activation process for the extension region 11 a, 11 b with a wide process window relating to the heat treatment process can be realized, and a high-performance transistor with a fine structure can easily be fabricated.

In the above descriptions of the semiconductor device and the fabrication method according to the sixth embodiment, the examples and effects have been described with attention paid to the n-channel insulated-gate transistor. Needless to say, the same advantageous effects can be obtained by applying the same techniques to the p-channel insulated-gate transistor.

(Seventh Embodiment)

Next, a semiconductor device and a method for fabricating the semiconductor device, according to a seventh embodiment of the invention, are described. In this embodiment, as in the first to sixth embodiments, the first conductivity type and second conductivity type are mutually opposite conductivity types. In the description of the seventh embodiment, it is assumed that the first conductivity type is p-type and the second conductivity type is n-type. Alternatively, the first conductivity type may be n-type and the second conductivity type may be p-type. FIG. 103 is a cross-sectional view of a semiconductor device according to the seventh embodiment.

As shown in FIG. 103, in the semiconductor device according to the seventh embodiment, the gate electrodes 78 n, 78 p in the structure shown in FIG. 101, which has been described in connection with the sixth embodiment, are replaced with gate electrodes 79 n, 79 p. Specifically, the gate electrodes 79 n, 79 p are formed of polycrystalline silicon or polycrystalline SiGe (Ge concentration: 10 to 30 atomic %) with a thickness of about 50 to 150 nm on the gate insulation films 73 n, 73 p, which are formed of SiO₂ or SiON.

A plurality of impurity elements with different atomic radii are implanted in the gate electrode 79 n. FIG. 104 is a table showing atomic radii of impurities of Group IV elements (in particular, Si, Ge) as covalent bond radii according to Pauli's principle. The unit is nm.

The impurities implanted in the gate electrode 79 n are a combination of an element of the major conductivity type (n-type, Group V) and an element of the opposite conductivity type (p-type, Group III) in the gate electrode 79 n. Specifically, at least one of B, Al, Ga and Tl, which are Group III elements, and at least one of P, As, Sb and Bi, which are Group V elements, are implanted in the gate electrode 79 n. At this time, it is preferable to set the concentration of the impurity element of the opposite conductivity type (n-type) at 10 to 70 atomic % of the concentration of the impurity element of the major conductivity type (p-type). FIG. 105 is a graph showing, for example, a gate depletion ratio and a gate leakage current, relative to the ratio of B to P, in a case where B (opposite conductivity type: p-type) and P (major conductivity type: n-type) are implanted in the gate electrode 79 n. As shown in FIG. 105, if the ratio of the impurity element of the opposite conductivity type to the impurity element of the major conductivity type decreases to 10 atomic % or less, the gate leakage current disadvantageously increases. On the other hand, if the ratio exceeds 70 atomic %, the gate depletion ratio increases although the gate leakage current is low, and thus this case is not preferable. Therefore, the range of 10 to 70 atomic % is preferable.

In addition, as regards the combination of impurities implanted in the gate electrode 79 n, it is preferable that the atomic radius of one of the impurity elements be greater (As, Al, Ga, Sb, Bi, Tl) than the atomic radius (r=0.117 nm) of Si, and the atomic radius of the other impurity element be less (B, P) than the atomic radius of Si. Examples of the preferable combination are B (p-type, r=0.088 nm) and Sb (n-type, r=0.136 nm); B and As (n-type, r=0.146 nm); and Al (p-type, r=0.126 nm) and P (n-type, r=0.110 nm).

The above description has been given of the case of the combination of n- and p-type impurities, but the plural impurity elements to be implanted in the gate electrode 79 n may be of the same conductivity type. In this case, it is preferable to meet the condition that the atomic radius of one of the impurity elements be greater than the atomic radius of Si and the atomic radius of the other impurity element be less than the atomic radius of Si. For example, a combination of Sb (r=0.136 nm) having a greater atomic radius than Si and P (r=0.110 nm) having a less atomic radius than Si, or a combination of Ga (r=0.126 nm) and B (r=0.088) may be adopted.

Further, a combination of an electrically inactive Group IV element and a Group V element may be adopted. For example, a combination of Sn (r=0.146 nm), which is a Group IV element, and P may be adopted. In this case, too, the n-type conductivity type may be used as the major conductivity type. Accordingly, a combination of Sn, P and Ga, for instance, may be adopted.

Also in the gate electrode 79 p, as in the gate electrode 79 n, a plurality of impurity elements having different atomic radii are implanted. The combination of impurities to be implanted has the same relationship as in the gate electrode 79 n.

For example, in the case of the combination of impurity elements of mutually opposite conductivity types, such as B (major conductivity type (p-type): r=0.088 nm) and As (opposite conductivity type (n-type): R=0.118 nm), it is preferable to set the concentration of the impurity element of the opposite conductivity type (n-type) at 10 to 70 atomic % of the concentration of the impurity element of the major conductivity type (p-type). The reason for this has been explained with reference to FIG. 105. That is, if the ratio of the impurity element of the opposite conductivity type (n-type) to the impurity element of the major conductivity type (p-type) decreases to 10 atomic % or less, the gate leakage current increases. On the other hand, if the ratio of the impurity element of the opposite conductivity type (n-type) to the impurity element of the major conductivity type (p-type) exceeds 70 atomic %, the gate depletion ratio increases.

Besides, a combination of impurity elements of the same conductivity type, such as B (r=0.088 nm) and Al (r=0.126 nm), may be adopted. Even in a combination of Sn, which is an electrically inactive Group IV element, and B, p-type conductivity may be used as the major conductivity type.

Sidewall spacers 21 n, 21 p are formed on side surfaces of the gate electrodes 79 n, 79 p having the above-described structure and the gate insulation films 73 n, 73 p. In the other structural aspects, the seventh embodiment is the same as the sixth embodiment.

Next, a semiconductor device fabrication method according to the seventh embodiment is described. The fabrication method according to this embodiment is substantially the same as the method of the first embodiment, except for the fabrication steps of the gate insulation films 73 n, 73 p and gate electrodes 79 n, 79 p.

To start with, as shown in FIG. 2 which has been described in connection with the first embodiment, after device isolation regions 4 are formed in the Si substrate 1, desired impurities are ion-implanted in regions corresponding to channel portions, and these regions are electrically activated and a p-well region 2 and an n-well region 3 are formed.

Next, gate insulation films 73 n, 73 p are formed of SiO₂ by thermal oxidation, or of SiON (N concentration in surface layer <15%) by LPCVD, on the surfaces of the p-well region 2 and n-well region 3. This fabrication step is common to the step in the sixth embodiment.

In a subsequent fabrication step similar to the step of FIG. 3, a gate electrode film 79 with a thickness of 50 to 150 nm, such as a polycrystalline Si film or polycrystalline SiGe (Ge concentration: 10 to 30 atomic %) film, is formed on the gate insulation film 73 n, 73 p by LPCVD. Specifically, the gate insulation film 5 in FIG. 3 corresponds to the gate insulation film 73 n, 73 p in the present embodiment, and the polycrystalline Si film 7 in FIG. 3 corresponds to the gate electrode film 79 in the present embodiment.

Next, in a subsequent fabrication step similar to the step of FIG. 3, a photoresist film 51 is formed on the n-well region 3. Using the photoresist film 51 as a mask, atoms of Group V, e.g., phosphorus (P) or arsenic (As), which become n-type impurities, are ion-implanted in the gate electrode film 79 on the p-well region 2 with a dosage of 1×10¹⁵ cm⁻² to 5×10¹⁵ cm⁻². Further, boron (B), which is impurities of the opposite conductivity type, are ion-implanted with a dosage of, e.g., 2×10¹⁵ cm⁻². By this step, the impurity element having a greater atomic radius than Si and the impurity element having a less atomic radius than Si are implanted in the gate electrode film 79 on the p-well region 2. Needless to say, the combination of impurities to be implanted is not limited to this example.

Then, as in the step of FIG. 4, a photoresist film 52 is formed on the p-well region 2. Using the photoresist film 52 as a mask, atoms of Group III, e.g., B, which become p-type impurities, are ion-implanted in the gate electrode film 79 on the n-well region 3 with a dosage of 4×10¹⁵ cm⁻² to 8×10¹⁵ cm⁻². Further, arsenic (As), which is impurities of the opposite conductivity type, are ion-implanted with a dosage of, e.g., 2×10¹⁵ cm⁻². By this step, the impurity element having a greater atomic radius than Si and the impurity element having a less atomic radius than Si are implanted in the gate electrode film 79 on the n-well region 3. Needless to say, the combination of impurities to be implanted is not limited to this example.

Subsequently, as in the step of FIG. 5, the gate electrode film 79 and the gate insulation film 73 n, 73 p are selectively processed (patterned) by successive RIE. Thereby, gate electrodes 79 n, 79 p are completed. Further, an annealing process is performed under a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6, preferably in a temperature range of 1100° C. or less. For example, RTA is conducted within a retention time of 10 seconds at 1000° C. to 1050° C. or spike RTA is conducted with a peak temperature set at 1000° C. to 1050° C. Thereby, the impurities, which are ion-implanted in the steps of FIGS. 2 to 4 are diffused uniformly in the entire gate electrode layer, of which the gate electrode 79 n for the nMOSFET and the gate electrode 79 p for the pMOSFET are formed, so that the diffusion may reach the interface with the gate insulation films 73 n, 73 p.

Subsequently, as in the step of FIG. 7, sidewall spacers 8 n, 8 p are formed on side surfaces of the gate electrode 79 n and gate insulation film 73 n and on side surfaces of the gate electrode 79 p and gate insulation film 73 p.

In the next fabrication step, as in the step of FIG. 8, using a photoresist film 53 formed on the n-well region 3, gate electrode 79 n and sidewall spacers 8 n as a mask, atoms of Group V, e.g., phosphorus (P), which become n-type impurities, are ion-implanted in the surface of the p-well region 2. By this ion implantation, the impurity ions of Group V atoms are also implanted in the gate electrode 79 n. The conditions for the ion implantation are an acceleration energy of 5 keV and a dosage of 3×10¹⁵ cm⁻². The photoresist film 53 is then removed.

Next, as in the step of FIG. 9, using a photoresist 54 formed on the p-well region 2, gate electrode 79 p and sidewall spacers 8 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. By this ion implantation, the impurity ions of Group III atoms are also implanted in the gate electrode 79 p. The conditions for the ion implantation are an acceleration energy of 2 keV and a dosage of 3×10¹⁵ cm⁻².

Next, the inactive source/drain regions formed in the steps of FIGS. 8 and 9 are activated. Specifically, by using a halogen lamp as a heat source, an activation annealing process for the inactive source/drain regions is performed. The condition for the activation annealing process is a heat treatment condition in the hatched region in the double-logarithmic graph of FIG. 6 and, for example, the annealing is conducted within 10 seconds at 1000° C. By this activation annealing process, as in the step of FIG. 10, source/drain regions 9 a, 9 b, 10 a and 10 b, which are spaced apart from end portions of the gate electrodes 79 n, 79 p and are in contact with the device isolation regions 4, are formed in the Si substrate 1. By this activation annealing process, the impurities, which are doped in the gate electrode 79 n, 79 p, can be diffused to the interface with the gate insulation film 73 n, 73 p, and crystal defects occurring in the Si substrate 1 due to ion implantation can be eliminated.

Thereafter, in the same step as shown in FIG. 11, the sidewall spacers 8 n and 8 p are removed by using hot phosphoric acid.

In the next step similar to the step of FIG. 12, using a photoresist film 55 formed on the p-channel insulated-gate transistor region and the gate electrode 79 n as a mask, atoms of Group V, e.g., arsenic (As), which become n-type impurities, are ion-implanted in the surface of the p-well region 2 on the surface of the Si substrate 1. The conditions for the ion implantation are an acceleration energy of 1.5 keV and a dosage of 1×10¹⁵ cm⁻². As a result, the impurity element of the major conductivity type (n-type) is finally doped in the gate electrode 79 n with a dosage of 5×10¹⁵ cm⁻² to 1×10¹⁶ cm⁻². The photoresist film 55 is then removed.

In the next step similar to the step of FIG. 13, using a photoresist film 56 formed on the p-well region 2 and the gate electrode 79 p as a mask, atoms of Group III, e.g., boron (B), which become p-type impurities, are ion-implanted in the surface of the n-well region 3. The conditions for the ion implantation are an acceleration energy of 0.3 keV and a dosage of 1×10¹⁵ cm⁻². As a result, the impurity element of the major conductivity type (p-type) is finally doped in the gate electrode 79 p with a dosage of 5×10¹⁵ cm⁻² to 1×10¹⁶ cm⁻². FIG. 14 shows the state immediately after the ion implantation. In this state, inactive shallow extension regions 111 a, 111 b, 112 a and 112 b are formed in regions in the Si substrate 1, which neighbor the gate electrodes 79 n and 79 p and the device isolation regions 4.

Subsequently, as in the steps of FIGS. 15 and 16, a silicon oxide film 13 and a silicon nitride film 14 are successively formed.

Thereafter, as in the step of FIG. 17, using a flashtube as a heat source, an activation annealing process is performed. For the activation annealing process, the relationship between the heat treatment temperature and heat treatment time, which is indicated in the hatched region in the double-logarithmic graph of FIG. 6, is preferable.

The subsequent fabrication steps are the same as those described in connection with the first embodiment. In the RTA in the semiconductor device fabrication method according to the seventh embodiment, the xenon flashtube is used as the light source for light radiation. Alternatively, it is possible to use, as the light source, for instance, any one of flashtubes using other rare gases, mercury and hydrogen, an arc discharge lamp, an excimer laser, an Ar laser, an N2 laser, a YAG laser, a titanium-sapphire laser, a CO laser, and a CO₂ laser.

FIG. 106 is a graph showing the relationship between gate leakage current and gate depletion ratio with respect to the n-channel insulated-gate transistor according to the present embodiment and a conventional n-channel insulated-gate transistor. In FIG. 106, black solid circle marks indicate the present embodiment, and white circle marks indicate the prior art.

As shown in FIG. 106, in the case of the prior art, if the gate leakage current is reduced to 1×10⁻⁵ A or less, which is a level of no problem, the gate depletion ratio rises to 5% or more.

By contrast, in the present embodiment, deterioration of the gate insulation film 73 n due to phosphorus (P) can be suppressed. Therefore, even if the dosage of P is high, the gate leakage current is low. As a result, good characteristics with a gate leakage current of 1×10⁻⁵ A or less and a gate depletion ratio of 1% or less can be obtained.

FIG. 107 is a graph showing the relationship between on-current and off-current in the n-channel insulated-gate transistor according to the seventh embodiment of the invention and the conventional n-channel insulated-gate transistor. FIG. 108 is a graph showing the relationship between gate length and gate threshold voltage in the n-channel insulated-gate transistor according to the seventh embodiment of the invention and the conventional n-channel insulated-gate transistor. In FIGS. 107 and 108, black solid circle marks indicate the present embodiment, and white circle marks indicate the prior art.

As shown in FIGS. 107 and 108, with the structure of the present embodiment, compared to the prior art, a higher driving power and good rolloff characteristics were obtained. In short, according to the semiconductor device fabrication method according to the seventh embodiment, a transistor with a fine structure and a high performance can be fabricated.

According to the semiconductor device fabrication method of the present embodiment, if impurities of the opposite conductivity type (p-type) are doped in the gate electrode 79 n, a remarkable improvement is observed, as shown in FIG. 105, in the gate depletion ratio/gate leakage current characteristics in the range of impurity density between 10 atomic % and 70 atomic % relative to the impurities of the major conductivity type (n-type). Preferably, if the impurity density is set between 30 atomic % and 60 atomic %, the MOS characteristics are stabilized and the non-uniformity in transistor characteristics can be reduced. The reason is as follows. With the increase in impurity density of boron (B) that is of the opposite conductivity type, the boron combines with P to form a III-V compound and stabilizes. Thus, even if high-concentration P is present, diffusion or permeation to the gate insulation film is suppressed and virtually no leakage path is formed. Hence, despite the impurity density of P in the gate polycrystalline Si being the same, the activation temperature can be raised. Therefore, the activation density of the gate electrode 79 n, source/drain region 9 a, 9 b and extension region 11 a, 11 b can be increased within such a range as not to increase gate leakage current, and the process window relating to the heat treatment process can be increased.

Thus, according to the semiconductor device fabrication method of the seventh embodiment, the activation process of the extension region 11 a, 11 b with a wide process window relating to the heat treatment step can be realized, and a high-performance transistor with a fine structure can easily be fabricated.

In the above descriptions of the semiconductor device and fabrication method according to the seventh embodiment, the examples and effects have been described with attention paid to the n-channel insulated-gate transistor. Needless to say, the same advantageous effects can be obtained by applying the same techniques to the p-channel insulated-gate transistor.

(Other Embodiments)

The embodiments of the present invention are not restricted to the first to seventh embodiments. Various alternative embodiments, as well as examples and techniques for implementation of the semiconductor device fabrication method according to the first embodiment, will be clear from the disclosure to a person skilled in the art.

In the description of the first to seventh embodiments, the CMOS structure has been described. However, the embodiments should not be interpreted to be restricted to the CMOS structure. Needless to say, the embodiments are also applicable to, for instance, the structure of a p-channel insulated-gate transistor alone, such as a pMOS integrated circuit, and to the structure of an n-channel insulated-gate transistor alone, such as a nMOS integrated circuit. Further, the invention is applicable to an integrated circuit including a bipolar transistor. Although it should be noted that the third and fourth embodiments are techniques relating to the adjustment of characteristics of the p-channel insulated-gate transistor and n-channel insulated-gate transistor, which are necessitated by microfabrication, these techniques are also applicable to an integrated circuit including a bipolar transistor.

As is understood from the description of the fifth to seventh embodiments, it is not necessary to restrictively apply the descriptions of the first to fourth embodiments to MOSFETs in narrow senses, such as a pMOSFET and an nMOSFET, wherein silicon oxide films are used as gate insulation films. For example, the invention is applicable to insulated-gate transistors in which insulation films, other than the silicon oxide films, are used as gate insulation films. Various insulation films, aside from the SiN film, Si₃N₄ film and SiON film as described in the fifth to seventh embodiments, are usable as such gate insulation films of insulated-gate transistors. A multilayer film, for example, a three-layer stacked film such as an ONO stacked film (silicon oxide film (SiO₂ film)/silicon nitride film (Si₃N₄ film)/silicon oxide film (SiO₂ film)), is also usable. For example, as a gate insulation film of the insulated-gate transistors according to the embodiments of the invention, usable is a single-layer film, which is selected from a strontium oxide (SrO) film with ∈_(r)=6, a silicon nitride film (Si₃N₄ film) with ∈_(r)=7, an aluminum oxide (Al₂O₃) film with ∈_(r)=8 to 11, a magnesium oxide (MgO) film with ∈_(r)=10, an yttrium oxide (Y₂O₃) film with ∈_(r)=16 to 17, a hafnium oxide (HfO₂) film with ∈_(r)=22 to 23, a zirconium oxide (ZrO₂) film with ∈_(r)=22 to 23, a tantalum oxide (Ta₂O₅) film with ∈_(r)=25 to 27 and a bismuth oxide (Bi₂O₃) film with ∈_(r)=40, or a composite stacked film of two or more of these films. Needless to say, the value of specific dielectric constant ∈_(r), exemplified above, is variable depending on fabrication methods, and may take a value deviating from the range of the above-exemplified values. Further, a composite film of a silicon oxide film and at least one of the above-listed films may be used. The composite film may comprise three or more stacked layers. Specifically, an insulation film, which includes at least a part of the above-mentioned material with a specific dielectric constant ∈_(r) of 5 to 6 or more, is preferable. In the case of the composite film, however, it is preferable to select a combination in which the effective specific dielectric constant ∈_(r), which is measured as the dielectric constant of the whole film, becomes 5 to 6 or more. An insulation film of a ternary compound, such as a hafnium aluminate (HfAlO) film, is usable. Specifically, an oxide including at least one of strontium (Sr), aluminum (Al), magnesium (Mg), yttrium (Y), hafnium (Hf), zirconium (Zr), tantalum (TA) and bismuth, or a silicon nitride including at least one of these elements, is usable as a gate insulation film of the insulated-gate transistors according to the embodiments of the invention. A ferroelectric material, such as strontium titanate (SrTiO₃) or barium strontium titanate (BaSrTiO₃), is usable as a high-dielectric-constant gate insulation film material, but, in this case, consideration should be given to deficiency in thermal stability at interface with polycrystalline Si and to hysteresis characteristics of ferroelectric material.

The semiconductor devices according to the embodiments of the invention are not limited to semiconductor integrated circuits such as LSIs. For example, the embodiments are applicable to an individual semiconductor device, for example, a microfabricated pMOSFET or nMOSFET, such as a terahertz-band high-frequency MOS transistor. Furthermore, the embodiments are applicable to the structure of a high-frequency power transistor in which a great number of microfabricated unit cells are arrayed on one chip, and a method for fabricating the same.

The profile of nitrogen concentration, which has been described in connection with the fifth embodiment, is not limited to the above-described example. FIG. 109 is a graph showing an impurity concentration profile in the first and second insulation films in a semiconductor device according to a first modification of the fifth embodiment. As shown in FIG. 109, it should suffice if the nitrogen concentration in the first gate insulation film is 30 atomic % or less, and if the nitrogen concentration in the second gate insulation film is 30 to 57 atomic %. These ranges are indicated by hatched regions in FIG. 109. Thus, for example, the nitrogen concentration may substantially be uniform in the first and second gate insulation films.

FIG. 110, like FIG. 109, is a graph showing an impurity concentration profile in a semiconductor device according to a second modification of the fifth embodiment. As shown in FIG. 110, the nitrogen concentration in the first and second gate insulation films may vary with a gradient (e.g., inverse proportion to depth). It should suffice if the nitrogen concentration in the gate insulation film falls within the hatched regions in FIGS. 109 and 110. The gate insulation film may be a multilayer film comprising three or more layers, or may be a single-layer film having a concentration profile which falls within the hatched regions.

FIG. 111 is a cross-sectional view of a semiconductor device according to a third modification of the fifth embodiment. In this modification, the fifth embodiment and the second embodiment are combined. Specifically, in the structure shown in FIG. 98, the offset spacers 6 n and 6 p, which have been described in connection with the second embodiment, may be provided.

FIG. 112 is a cross-sectional view of a semiconductor device according to a fourth modification of the fifth embodiment. In this modification, the fifth embodiment and the third embodiment are combined. Specifically, in the structure shown in FIG. 98, the offset spacers 6 n, which have been described in connection with the third embodiment, may be provided in the nMOSFET. In this case, no offset spacer is provided in the pMOSFET.

FIG. 113 is a cross-sectional view of semiconductor device according to a fifth modification of the fifth embodiment. In this modification, the fifth embodiment and the fourth embodiment are combined. Specifically, in the structure shown in FIG. 98, the offset spacers 6 na and 6 pa, which have been described in connection with the fourth embodiment, may be provided. Needless to say, the relationship in thickness between the offset spacers 6 na and 6 pa is:

offset spacer 6 na>offset spacer 6 pa.

FIG. 114 is a cross-sectional view of a semiconductor device according to a first modification of the sixth embodiment. In this modification, the sixth embodiment and the second embodiment are combined. Specifically, in the structure shown in FIG. 101, the offset spacers 6 n and 6 p, which have been described in connection with the second embodiment, may be provided.

FIG. 115 is a cross-sectional view of a semiconductor device according to a second modification of the sixth embodiment. In this modification, the sixth embodiment and the third embodiment are combined. Specifically, in the structure shown in FIG. 101, the offset spacers 6 n, which have been described in connection with the third embodiment, may be provided in the nMOSFET. In this case, no offset spacer is provided in the pMOSFET.

FIG. 116 is a cross-sectional view of a semiconductor device according to a third modification of the sixth embodiment. In this modification, the sixth embodiment and the fourth embodiment are combined. Specifically, in the structure shown in FIG. 101, the offset spacers 6 na and 6 pa, which have been described in connection with the fourth embodiment, may be provided. Needless to say, the relationship in thickness between the offset spacers 6 na and 6 pa is:

offset spacer 6 na>offset spacer 6 pa.

FIG. 117 is a cross-sectional view of a semiconductor device according to a fourth modification of the sixth embodiment. In this modification, the sixth embodiment and the fifth embodiment are combined. Specifically, in the structure shown in FIG. 101, the gate insulation film 73 n may be replaced with the stacked structure of the first gate insulation film 71 n and second gate insulation film 72 n, which has been described in connection with the fifth embodiment, and the gate insulation film 73 p may be replaced with the stacked structure of the first gate insulation film 71 p and second gate insulation film 72 p, which has been described in connection with the fifth embodiment. In addition, in the structure shown in FIG. 117, the offset spacers 6 n and 6 p, which have been described in connection with the second to fourth embodiments, may be provided.

FIG. 118 is a cross-sectional view of a semiconductor device according to a first modification of the seventh embodiment. In this modification, the seventh embodiment and the second embodiment are combined. Specifically, in the structure shown in FIG. 103, the offset spacers 6 n and 6 p, which have been described in connection with the second embodiment, may be provided.

FIG. 119 is a cross-sectional view of a semiconductor device according to a second modification of the seventh embodiment. In this modification, the seventh embodiment and the third embodiment are combined. Specifically, in the structure shown in FIG. 103, the offset spacers 6 n, which have been described in connection with the third embodiment, may be provided in the nMOSFET. In this case, no offset spacer is provided in the pMOSFET.

FIG. 120 is a cross-sectional view of a semiconductor device according to a third modification of the seventh embodiment. In this modification, the seventh embodiment and the fourth embodiment are combined. Specifically, in the structure shown in FIG. 103, the offset spacers 6 na and 6 pa, which have been described in connection with the fourth embodiment, may be provided. Needless to say, the relationship in thickness between the offset spacers 6 na and 6 pa is:

offset spacer 6 na>offset spacer 6 pa.

FIG. 121 is a cross-sectional view of a semiconductor device according to a fourth modification of the seventh embodiment. In this modification, the seventh embodiment and the fifth embodiment are combined. Specifically, in the structure shown in FIG. 103, the gate insulation film 73 n may be replaced with the stacked structure of the first gate insulation film 71 n and second gate insulation film 72 n, which has been described in connection with the fifth embodiment, and the gate insulation film 73 p may be replaced with the stacked structure of the first gate insulation film 71 p and second gate insulation film 72 p, which has been described in connection with the fifth embodiment. In addition, in the structure shown in FIG. 121, the offset spacers 6 n and 6 p, which have been described in connection with the second to fourth embodiments, may be provided.

FIG. 122 is a cross-sectional view of a semiconductor device according to a fifth modification of the seventh embodiment. In this modification, the seventh embodiment and the sixth embodiment are combined. Specifically, in the structure shown in FIG. 103, atomic nitrogen may be doped in the gate electrodes 79 n and 79 p. Arrows in FIG. 122 indicate that the gate electrodes 79 n and 79 p contain atomic nitrogen. The nitrogen concentration at this time is set as described in connection with the sixth embodiment. In the structure shown in FIG. 122, the offset spacers 6 n and 6 p, which have been described in connection with the second to fourth embodiments, may be provided, and the gate insulation film 73 n, 73 p may be formed to have the multilayer structure as described in connection with the fifth embodiment.

Additional advantages and modifications will readily occur to those skilled in the art. Therefore, the invention in its broader aspects is not limited to the specific details and representative embodiments shown and described herein. Accordingly, various modifications may be made without departing from the spirit or scope of the general inventive concept as defined by the appended claims and their equivalents. 

1. A method for fabricating a semiconductor device comprising: forming a gate insulating film on a semiconductor region of a first conductivity type; forming a polycrystalline semiconductor layer on the gate insulating film; selectively etching the polycrystalline semiconductor layer to form a gate electrode pattern; forming a sidewall spacer on a side surface of the gate electrode pattern; injecting an ion of a first impurity element of a second conductivity type into the semiconductor region in self-alignment with the gate electrode pattern, before forming the sidewall spacer or after removing the sidewall spacer; activating the ion of the first impurity element by first annealing; injecting an ion of a second impurity element of the second conductivity type into the semiconductor region in self-alignment with the gate electrode pattern and the sidewall spacer, with the sidewall spacer formed on the side surface of the gate electrode pattern; and activating the ion of the second impurity element by second annealing, wherein a channel region is formed in a portion of the semiconductor region immediately below a gate electrode, wherein a source extension region and a drain extension region of the second conductivity are formed in a portion of the semiconductor region by the first impurity element, the source extension region and the drain extension region each having a junction depth which is less than or equal to 20 nm, the channel region being sandwiched between the source extension region and the drain extension region, wherein a source region of the second conductivity type is connected to one end of the source extension region, the one end of the source extension region being located farther from the channel region than another end thereof, the source region having a junction depth which is greater than the junction depth of the source extension region, wherein a drain region of the second conductivity type is connected to one end of the drain extension region, the one end of the drain extension region being located farther from the channel region than another end thereof, the drain region having a junction depth which is greater than the junction depth of the drain extension region, and wherein the first and second annealing are performed at a temperature ranging from 1273 K to 1600 K and for a time period on a double-logarithmic graph with an upper limit expressed by an equation (1) and a lower limit expressed by an equation (2): t=3×10⁻¹⁵ exp(49000/T)  (1), and t=3×10⁻¹⁷ exp(49000/T)  (2), where t represents a time period for the first and second annealing and T represents a temperature of the first and second annealing.
 2. The method according to claim 1, wherein the first and second impurity elements are injected into the gate electrode and diffused to an interface between the gate electrode and the gate insulating film in a concentration between 1×10²⁰ cm⁻³ and 5×10²⁰ cm⁻³.
 3. A method for fabricating a semiconductor device comprising: forming gate insulating films on an n-type semiconductor region and a p-type semiconductor region on a semiconductor substrate; forming a polycrystalline semiconductor layer on the gate insulating films; selectively etching the polycrystalline semiconductor layer to form an n-channel gate electrode pattern and a p-channel gate electrode pattern; forming a first sidewall spacer on a side surface of the n-channel gate electrode pattern and a second sidewall spacer on a side surface of the p-channel gate electrode pattern; injecting an ion of a first n-type impurity element to the p-type semiconductor region in self-alignment with the n-channel gate electrode pattern, before forming the first sidewall spacer or after removing the first sidewall spacer; injecting an ion of a first p-type impurity element into the n-type semiconductor region in self-alignment with the p-channel gate electrode pattern, before forming the second sidewall spacer or after removing the second sidewall spacer; activating the ion of the first n-type impurity element and the ion of the first p-type impurity element by first annealing; injecting an ion of a second n-type impurity element into the p-type semiconductor region in self-alignment with the n-channel gate electrode pattern and the first sidewall spacer, with the first sidewall spacer formed on the side surface of the n-channel gate electrode pattern; injecting an ion of a second p-type impurity element into the n-type semiconductor region in self-alignment with the p-channel gate electrode pattern and the second sidewall spacer, with the second sidewall spacer formed on the side surface of the p-channel gate electrode pattern; and activating the ion of the second n-type impurity element and the ion of the second p-type impurity element by second annealing, wherein a first channel region is formed in a portion of the p-type semiconductor region immediately below an n-channel gate electrode, wherein a second channel region is formed in a portion of the n-type semiconductor region immediately below a p-channel gate electrode, wherein an n-type source extension region and an n-type drain extension region are formed in a portion of the p-type semiconductor region, the n-type source and drain extension regions each having a junction depth which is less than or equal to 20 nm, the first channel region being sandwiched between the n-type source extension region and the n-type drain extension region, wherein a p-type source extension region and a p-type drain extension region are formed in a portion of the n-type semiconductor region, the p-type source and drain extension regions each having a junction depth which is less than or equal to 20 nm, the second channel region being sandwiched between the p-type source extension region and the p-type drain extension region, wherein an n-type source region is connected to one end of the n-type source extension region, the one end of the n-type source extension region being located farther from the first channel region than another end thereof, the n-type source region having a junction depth which is greater than the junction depth of the n-type source extension region, wherein an n-type drain region is connected to one end of the n-type drain extension region, the one end of the n-type drain extension region being located farther from the first channel region than another end thereof, the n-type drain region having a junction depth which is greater than the junction depth of the n-type drain extension region, wherein a p-type source region is connected to one end of the p-type source extension region, the one end of the p-type source extension region being located farther from the second channel region than another end thereof, the p-type source region having a junction depth which is greater than the junction depth of the p-type source extension region, wherein a p-type drain region is connected to one end of the p-type drain extension region, the one end of the p-type drain extension region being located farther from the second channel region than another end thereof, the p-type drain region having a junction depth which is greater than the junction depth of the p-type drain extension region, and wherein the first and second annealing are performed at a temperature ranging from 1273 K to 1600 K, and for a time period on a double-logarithmic graph with an upper limit expressed by an equation (1) and a lower limit expressed by an equation (2): t=3×10⁻¹⁵ exp(49000/T)  (1), and t=3×10⁻¹⁷ exp(49000/T)  (2), where t represents a time period for the first and second annealing and T represents a temperature of the first and second annealing.
 4. The method according to claim 3, wherein the first and second n-type impurity elements are injected into the n-type gate electrode and diffused to an interface between the n-channel gate electrode and the gate insulating film in a concentration between 1×10²⁰ cm⁻³ and 5×10²⁰ cm⁻³, and wherein the first and second p-type impurity elements are injected into the p-type gate electrode and diffused to an interface between the p-channel gate electrode and the gate insulating film in a concentration between 1×10²⁰ cm⁻³ and 5×10²⁰ cm⁻³.
 5. The method according to claim 3, wherein an overlap capacitance between the n-type drain extension region and the n-channel gate electrode is lower than an overlap capacitance between the p-type drain extension region and the p-channel gate electrode.
 6. The method according to claim 3, wherein the gate insulating films include a first gate insulating film under the n-channel gate electrode and a second gate insulating film under the p-channel gate electrode, wherein the first gate insulating film or the second gate insulating film includes a first film and a second film on the first film, wherein the first film is formed of silicon oxide film or silicon oxide nitride film with a nitrogen concentration of 15 atomic %, and wherein the second film includes nitrogen with a concentration of 20 to 57 atomic %.
 7. The method according to claim 3, wherein the n-channel gate electrode includes an n-type impurity element and a p-type impurity element, and wherein the p-type impurity element has a concentration of 10 to 70 atomic % of a concentration of the n-type impurity element.
 8. The method according to claim 7, wherein the n-type impurity element included in the n-channel gate electrode is Sb (antimony), As, or P, and wherein the p-type impurity included in the n-channel gate electrode is As or Al.
 9. The method according to claim 3, wherein the p-channel gate electrode includes an n-type impurity element and a p-type impurity element, and wherein the n-type impurity element has a concentration of 10 to 70 atomic % of a concentration of the p-type impurity element.
 10. The method according to claim 3, further comprising forming an offset spacer between the n-channel gate electrode pattern and the first sidewall spacer, wherein the ion of the first n-type impurity element is injected into the p-type semiconductor region in self-alignment with the n-channel gate electrode pattern and the offset spacer, and wherein the ion of the second n-type impurity element is injected into the p-type semiconductor region in self-alignment with the n-channel gate electrode pattern, the offset spacer, and the first sidewall spacer with the offset spacer and the first sidewall spacer formed on the side surface of the n-channel gate electrode.
 11. The method according to claim 3, further comprising: forming a first offset spacer between the n-channel gate electrode pattern and the first sidewall spacer; and forming a second offset spacer, different in a thickness from the first offset spacer, between the p-channel gate electrode pattern and the second sidewall spacer; wherein the ion of the first n-type impurity element is injected into the p-type semiconductor region in self-alignment with the n-channel gate electrode pattern and the first offset spacer, wherein the ion of the first p-type impurity element is injected into the n-type semiconductor region in self-alignment with the p-channel gate electrode pattern and the second offset spacer, wherein the ion of the second n-type impurity element is injected into the p-type semiconductor region in self-alignment with the n-channel gate electrode pattern, the first offset spacer, and the first sidewall spacer with the first offset spacer and the first sidewall spacer formed on the side surface of the n-channel gate electrode, and wherein the ion of the second p-type impurity element is injected into the n-type semiconductor region in self-alignment with the p-channel gate electrode pattern, the second offset spacer, and the second sidewall spacer with the second offset spacer and the second sidewall spacer formed on the side surface of the p-channel gate electrode.
 12. The method according to claim 3, wherein As (arsenic) is doped in the n-type source extension region and the n-type drain extension region as an impurity element, and wherein As and P (phosphorous) are doped in the n-type source region and the n-type drain region.
 13. The method according to claim 3, wherein the gate insulating films include a first gate insulating film under the n-channel gate electrode and a second gate insulating film under the p-channel gate electrode, and wherein the first gate insulating film is formed of an oxide or silicon nitride film including at least one of Sr (strontium), Al (aluminum), Mg (magnesium), Y (yttrium), Hf (hafnium), Zr (zirconium), Ta (tantalum), and Bi (bismuth).
 14. The method according to claim 3, wherein the gate insulating films include a first gate insulating film under the n-channel gate electrode and a second gate insulating film under the p-channel gate electrode, and wherein the second gate insulating film is formed of an oxide or silicon nitride film including at least one of Sr (strontium), Al (aluminum), Mg (magnesium), Y (yttrium), Hf (hafnium), Zr (zirconium), Ta (tantalum), and Bi (bismuth).
 15. The method according to claim 3, wherein the first annealing and the second annealing are each flash lamp annealing or laser annealing.
 16. The method according to claim 15, wherein the upper limit of the time range of the first annealing or the second annealing is 100 msec and expressed by the equation (2).
 17. The method according to claim 15, wherein the first annealing or the second annealing is performed with an insulating film formed on the n-channel gate electrode pattern, the p-channel gate electrode pattern, the p-type semiconductor region, and the n-type semiconductor region.
 18. The method according to claim 15, wherein the first annealing or the second annealing is performed with auxiliary heating of 400 to 900 degree Celsius. 